Crosslinking of Vinylidene Fluoride-Containing Fluoropolymers
A. Taguet,B. Ameduri,B. Boutevin
DOI: https://doi.org/10.1007/b136245
2005-01-01
Abstract:Fluoropolymers are well-known for their good properties in terms of chemical, thermal and electricalstabilities, inertness to acids, bases, solvents and oils, and high resistance to ageing and oxidation.Polyvinylidene fluoride (PVDF) is useful as a homopolymer endowed with interesting characteristics.It contains a high crystallinity rate, but is base sensitive. In addition, VDF can be co- orterpolymerized with several fluorinated monomers, rendering them suitable as elastomers and variousexamples of synthesis of VDF-copolymers are also presented. This review also focusses on binary andtertiary systems containing VDF. Several curing systems for these VDF-containing copolymers have beeninvestigated, especially diamines and their derivatives, aromatic polyhydroxy compounds, peroxideswith coagents, such as triallylisocyanurate, radiations, and thiol-ene systems. The best vulcanizateproperties are obtained by a two-step process. First, the material is press cured at differenttimes and temperatures, then, it is post cured in air or under nitrogen at higher temperature andtime, and under atmospheric pressure. Poly(VDF-co-HFP) copolymerscan react with primary, secondary or tertiary monoamines, but they are mainly crosslinked by diaminessuch as hexamethylene diamine (HMDA), their carbamates (HMDA-C), and derivatives. A mechanismof crosslinking is identified by Infrared and 19F NMR spectroscopies, andwas evidenced to proceed in three main steps. First, a VDF unit undergoes a dehydrofluorinationin the presence of the diamine, then the Michael addition occurs onto the double bonds to form crosslinking,while HF is eliminated from crosslinks in the presence of HF scavengers. The crosslinking mechanismwith bisphenols takes place also in three main steps (dehydrofluorination, then substitution of a fluorineatom by a bisphenol, and elimination of HF). The most efficient crosslinking bisphenol is bisphenolAF . A fluoropolymer crosslinked with peroxide/coagent systems needs to be functionalized orhalogenated to insure a free radical attack from peroxide. The peroxide is introduced with a coagentthat enhances the crosslinking efficiency, and the most efficient one is triallylisocyanurate (TAIC).The crosslinking mechanism of the peroxide/triallylisocyanurate system proceeds in three main steps.The crosslinking reaction occurs from a macroradical arising from the functional or halogenatedpolymer which is added onto the three double bonds of the TAIC. A fourth way to crosslink VDF-basedfluoropolymers deals with high energy radiation, such as X and γ (60Coor 137Cs)-rays, and charged particles (β-particles and electrons).Three different reactions are possible after irradiation of a PVDF, and the one that leads tocrosslinking is the recombination between two macroradicals. The irradiation dose used on the VDF-basedcopolymer has an influence on the thermal and mechanical properties. Finally, a crosslinkingsystem also used to vulcanizate hydrogenated elastomers concerns a thiol-ene system which requiresa mercapto function born by the VDF-based polymer. Crosslinking occurs via a non-conjugateddiene. The mechanical properties (tensile strength, elongation at break, hardness, elongation modulus,compression set resistance …) of the three main crosslinking systems of fluoroelastomers arecompared. Finally, the main applications of crosslinked VDF-based fluoropolymers are summarized whichinclude tubing in the aircraft building industry, sealing, tube or irregular-profile items of anydimension, films with good adhesion to metallic or rigid surfaces, multilayer insulator systems forelectrical conductors, captors, sensors, and detectors, and membranes for electrochemical applications.