Multilayer Core-Sheath Wires with Cus Nanosheet Arrays and Pedot Sheaths for High-Performance Fiber-Shaped Asymmetric Supercapacitors

Mingzhou Chen,Wei Cao,Xiaomin Zhang,Xinjuan Liu,Yuhua Xue

DOI: https://doi.org/10.2139/ssrn.4264091

2022-01-01

SSRN Electronic Journal

Abstract:The performance of supercapacitors is seriously affected by the framework of electrodes, the intrinsic properties of active materials, as well as the mutual connection between the active materials and the current collectors. Here, a design strategy for binder-free multilayer core-sheath structures was proposed to synthesize two novel high-performance composite electrodes (PEDOT@CTNT and CuS@CTNT). These core-sheath composite electrodes contain three layers of different materials, where titanium wire in the inner core acted as the current collector, titanium dioxide nanotube arrays deposited with carbon in the middle layer could construct the nanoarchitecture, and active materials including CuS nanosheet arrays and PEDOT are in the outer sheath layer. These unique core-sheath wires exhibit excellent energy storage performance because of the synergy between the materials in each layer gives. The capacitance of the PEDOT@CTNT core-sheath wire is up to 191.63 mF cm-2 at a current density of 1 mA cm-2. The PEDOT@CTNT and CuS@CTNT core-sheath wires are further used as electrodes to assemble all-solid-state asymmetric fiber-shaped supercapacitors (AFSCs). The as-prepared AFSCs have a wide potential window of 2.4 V, a good specific areal capacitance of 63.09 mF cm−2 at the current density of 0.5 mA cm-2, and an excellent energy density of 22.43 μWh cm−2. The AFSCs also exhibit ultralong cycling lifespan with retaining 81.18% capacitance of the initial value after 12000 charging and discharging cycles.