Abstract:The southern China is located in high-temperature and high-humidity areas with long and high rainfall. Affected by the sea breeze, the salt on the surface of Composite insulators in the area is higher than others. If the insulator is damaged and exposed to continuous rain, there may be a consistent arc on the surface of the insulator due to electric field distortion caused by insulator's damage. To explore the effect of continuous arc on the properties of silicone rubber materials operating on natural environment, we chose four groups of the silicon rubber samples with different contents of ATH and silica and coat them with kaolin in order to simulate natural pollution. Insulators were placed in the tracking test apparatus, the voltage of 2.5 kV, 3.5 kV, 4.5 kV, 6 kV and the corresponding current velocity were applied to simulate the actual aging process according to the relevant passage. Transverse relaxation time and residual mass were measured respectively, also hardness, lightness and static contact angle of the samples were carried out after the test. The result shows that transverse relaxation time and residual mass of silicone rubber decreased with the increase of accelerated aging time. If the residual mass decreases to a certain value, the silicone rubber material sample cannot continue to run while discharge is concentrated in a certain area on the surface of silicone rubber. After the aging process, lightness and static contact of the sample decreased, and hardness changed little. At the same time, it can find that the higher the relative content of ATH and silica, the better the performance of silicone rubber under the action of continuous arc when the rubber content reaches a certain proportion by comparing the properties of silicone rubber with different component.

Experimental Study on Flashover and Wetting Characteristics of Silicone Rubber Sheet under Different Humidity

Study of DC Arc Characteristics on Polluted Silicon Rubber Surface

Study on Discharge of Silicone Rubber Composite Insulator Surface Attached with Water Droplets Based on Experiment and Electrostatic Field Simulation

Effect of superhydrophobicity on flashover characteristics of silicone rubber under wet conditions

Influence of Environmental Factors on Hydrophobicity Transfer Property of Silicone Rubber Material

Flashover Performance of Silicon Rubber under Combined AC-DC Voltage and Its Improving Method

The effect of dynamic behaviours of the water droplet on DC/AC flashover performance on silicone rubber surface: Experiment, simulation and theoretical analysis

Research on the Influence of Consistent Arc on Performance of Composite Insulators in Areas of High Temperature and High Humidity

Frequency Characters of Leakage Current on the Surface of Outdoor Insulators in Different Relative Humidity

Experimental Study on the Pollution Flashover Mechanism of Polymer Insulators

Flashover characteristics of a droplet impacting the silicone rubber surface

Flashover Characteristic of Polluted Silicone Rubber with Different Hydrophobicity

Influence of Temperature Difference on Wetting Characteristics of Insulators

Effect of Temperature and Humidity on the Surface Charge Decay of Silicone Rubber

A Study on the Discharge along RTV Coated Insulators

Research on the Material and Pollution-Flashover Properties of Hard Composite Insulators

Characteristics of Streamer Propagation along the Insulation Surface: Influence of Air Pressure and Humidity

Flashover characteristics of discrete water droplets on the surface of super-hydrophobic silicone rubber

Influence Mechanisms of Ultraviolet Irradiation Aging on Dc Surface Discharge Properties of Silicone Rubber in Dry and Humid Air

Wetting Characteristics of the Hydrophobic Material Surface Through Condensation

Dynamic Behavior of Water Droplets and Flashover Characteristics on a Superhydrophobic Silicone Rubber Surface