Cobalt–aluminum Oxide Clusters-Embedded Γ-Al2o3 Nanosheets for Peroxymonosulfate Activation: Interfacial Ph-Buffering Property to Eliminate Cobalt Leaching and Boost the Catalytic Activity

Ding Liu,Zhenkun Su,Bo Han,Kaisheng Xia,Chenggang Zhou,Qiang Gao
DOI: https://doi.org/10.1016/j.apcatb.2023.122555
2023-01-01
Abstract:Cobalt-aluminum oxide clusters-embedded & gamma;-Al2O3 nanosheets (CAO@AO) were facilely fabricated and developed for peroxymonosulfate (PMS) activation. Interestingly, the Al-OH-rich amphiphilic surface of CAO@AO endowed the catalyst with unique interfacial pH-buffering property, which stabilized the reaction media at nearly neural level and thus prevented the cobalt sites from leaching. Moreover, the presence of Al-OH groups around the Co Al oxide clusters facilitated the activation of PMS and the redox cycle of Co2+/Co3+, which resulted in a boosted catalytic activity. Consequently, the CAO@AO exhibited zero leaching of cobalt and high efficacy for PMS activation, enabling complete and ultrafast removal of metronidazole with a significantly higher turnover frequency (TOF, 1.83 min 1) than that of Co3O4 (0.004 min 1). It was also demonstrated that introducing suitable foreign metal into CAO@AO could further enhance the catalytic activity (e.g., TOF of Mn(40%)CAO@AO: 5.80 min 1). Furthermore, Mn(40%)-CAO@AO-decorated granular support was synthesized that dominated a continuous-flow degradation in column reaction system.
What problem does this paper attempt to address?