Plasma-Assisted Synthesis of Defect-Rich O and N Codoped Carbon Nanofibers Loaded with Manganese Oxides as an Efficient Oxygen Reduction Electrocatalyst for Aluminum–Air Batteries
Ruiqi Cheng,Fei Wang,Min Jiang,Kaiqi Li,Tianshuo Zhao,Pengyu Meng,Jian Yang,Chaopeng Fu
DOI: https://doi.org/10.1021/acsami.1c09067
2021-07-31
Abstract:The oxygen reduction reaction (ORR) with sluggish kinetics on the cathode of aluminum–air (Al–air) batteries greatly limits their further development. Here, a new strategy is proposed to synthesize oxygen and nitrogen codoped carbon nanofibers loaded with manganese oxides (MnO/Mn2O3/ONCNF-n) as an efficient electrocatalyst for ORR by using oxygen plasma surface etching. The MnO/Mn2O3/ONCNF-3 exhibit superior ORR performance in an alkaline electrolyte, which is attributed to various active sites including N and O heteroatoms, vacancies, and manganese oxides. Additionally, the fabricated homemade Al–air battery (AAB) with MnO/Mn2O3/ONCNF-3 exhibits a maximum power density of 129.7 mW cm–2, demonstrating comparable performance to AABs based on the commercial Pt/C catalyst. This work provides a new approach of using O2 plasma for enhancing the ORR catalytic activities of carbon materials.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c09067.Synthesis of reference groups, RRDE measurements, FTIR, nitrogen adsorption isotherms, SEM images, HAADF–STEM images with elemental mapping, EDS line-scan spectrum, FFT pattern, XPS characterizations of the reference groups, LSV curves of the reference groups (MnxOy, MnxOy-3, NCNF, and ONCNF-3), EIS analysis of MnO/Mn2O3/ONCNF-n, chronoamperometric response of the MnO/Mn2O3/ONCNF-3, CV, LSV, Tafel slope, peroxide yield and electron-transfer number of MnO/Mn2O3/ONCNF-n in 3.5% NaCl neutral electrolyte, extracted values of Eonset and E1/2 in alkaline/neutral electrolyte, and comparison of ORR and battery performances (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology