Study on gradient structure constructed by rapid heat treatment of ultrafine bainitic steel

LIU Changbo,SUN Dongyun,LI Yanguo,LONG Xiaoyan,YANG Zhinan,ZHANG Fucheng

DOI: https://doi.org/10.13228/j.boyuan.issn1001-0963.20220095

2023-01-01

Abstract:Steel with high core toughness and high surface hardness is an important requirement for key component such as impact load resistant bearings and gears. The ultrafine bainite steel was subjected to local rapid heat treatment to obtain the gradient structure with high surface hardness and high core toughness. The phase transformation behavior of ultrafine bainite during rapid heat treatment, as well as the gradient microstructure and properties were studied. The results show that the retained austenite in the ultrafine bainitic steel is decomposed into ferrite and carbide, and the bainitic ferrite coarsens during the rapid heating process. Moreover, there is obvious phase transformation lag during the rapid heating process. After rapid heat treatment, a gradient structure of microstructure and properties is formed between the local heating zone and the matrix. Martensite and retained austenite obtained by quenching process constitute hardened zone structure. With the increase in depth, the volume fraction of martensite decreases, and the tempering products of initial ultrafine bainite increase. The hardness of hardened zone is as high as 63HRC, which gradually decreases to 38HRC. With the increase in depth, the hardness decreases by about 6HRC compared with that of the matrix.