Abstract:While Portland cement produces large amounts of carbon dioxide, low-calcium high-strength cements effectively reduce carbon emissions by decreasing the proportion of high-calcium minerals. In order to enhance the practical application value of low-calcium high-strength cement, the effects of mineral admixtures on the chloride binding capacity and pore structure characteristics of low-calcium high-strength cement pastes were investigated by equilibrium method and mercury intrusion method. The results showed that the chloride binding capacity of low-calcium high-strength cement pastes is superior to that of Portland cement. Fly ash and slag enhance this capacity by promoting monosulfoaluminate and C-S-H gel formation, with fly ash being more effective. Ground limestone also boosts chloride binding when incorporated at less than 10 wt%. However, sulfates have a more significant negative impact on chloride binding capacity in low-calcium high-strength cement pastes compared to Portland cement. The porosity of low-calcium high-strength cement pastes exhibits contrasting trends with the addition of fly ash, ground limestone, and slag. Fly ash and limestone initially coarsen the pore structure but later facilitate the transition of larger pores to smaller ones. In contrast, slag initially has little impact but later promotes the conversion of large capillary pores to medium ones, optimizing the pore structure. Notably, above 10 wt% fly ash, the critical pore diameter decreases with additional fly ash except at 10% where it increases for 3 days. Ground limestone enlarges the critical pore diameter, and this effect intensifies with higher content. During early hydration, slag decreases the critical pore diameter, but its impact diminishes in later stages.

Corrosion Mechanism of Reinforcement in LC3 Cement Pastes under Coupled Carbonation and Chloride Attack

Chloride-induced Corrosion Patterns of Reinforcements in Simulated Pore Solutions of Calcium Sulfoaluminate Cement Concrete: an Analytical Study

Calcined Clay and Limestone as Partial Replacements of Portland Cement: Electrochemical Corrosion Behavior of Low Carbon Steel Rebar as Concrete Reinforcement in Corrosive Environment

Effects of Chloride Ion Binding on Microstructure of Cement Pastes

Effect of natural carbonation on chloride binding behaviours in OPC paste investigated by a thermodynamic model

Development of Limestone Calcined Clay Cement Concrete in South China and Its Bond Behavior with Steel Reinforcement

Chloride transport resistance of alkali-activated concrete exposed to combined chloride, sulfate and carbonation environment

Steel Corrosion Behavior of Reinforced Calcium Aluminate Cement-Mineral Additions Modified Mortar

Microstructure, Hydration, and Chloride Binding Behavior of Limestone Calcined Clay Cement Prepared Using Seawater

Experimental studies on durability performances of ultra-lightweight low-carbon LC3 cement composites against chloride ingression and carbonation

Early Strength-Promoting Mechanism of Inorganic Salts on Limestone-Calcined Clay Cement

Influence of Magnesium Oxide on Carbonation of Cement Paste Containing Limestone and Metakaolin

Chloride erosion resistance of calcium formate incorporated cement mortar under chloride attack

Performance of Limestone Calcined Clay Cement (LC3) with various kaolinite contents with respect to chloride transport

Chloride-related Steel Corrosion Initiation in Cement Paste Prepared with the Incorporation of Blast-Furnace Slag

Chloride Binding Behavior and Pore Structure Characteristics of Low-Calcium High-Strength Cement Pastes

Effect of Carbonation on Release of Bound Chlorides in Chloride-Contaminated Concrete

Thermodynamic Study on Phase Composition of Hardened Portland Cement Paste Exposed to Cacl2 Solution: Effects of Temperature, Cacl2 Concentration, and Type and Dosage of Supplementary Cementitious Materials

Effect of limestone powder addition on threshold chloride concentration for steel corrosion in reinforced concrete

Study on the Mechanism of Early Strength Strengthening and Hydration of LC3 Raised by Shell Powder

Chloride Binding Capacity and Phase Modification of Alumina Compound Blended Cement Paste under Chloride Attack