Study on the electromagnetic properties and microwave absorption properties of Co 2 Si by non-magnetic metal Cu and Mn single doping
Jiang Zou,Quan Xie,Jing Chen,Bo Wang,Yu Zhang
DOI: https://doi.org/10.1016/j.materresbull.2024.113004
IF: 5.6
2024-07-26
Materials Research Bulletin
Abstract:In this study, Co 2 Si and Co 2 Si-doped powder materials with different Cu,Mn proportions were prepared by mechanical alloying and thermal sintering. The effects of Cu,Mn doping on the crystal structure, magnetic properties, and microwave absorption properties of Co 2 Si were investigated. The results showed that all the sample peaks obtained by XRD measurement were consistent with the standard card (ICDD: 98-005-2281) of Co 2 Si.The Ms values corresponding to 2 wt%, 4 wt%, and 8 wt% Cu doping were 25.79 emu/g, 23.79 emu/g, and 21.75 emu/g, respectively. The saturation magnetization of Co 2 Si samples doped with 2 at%, 4 at% and 8 at% Mn was 8.26 emu/g, 20.33 emu/g and 14.65 emu/g, respectively.The doping of Cu significantly improved the comprehensive absorption performance of Co 2 Si alloy, and the lowest reflection loss was obtained when Cu was doped with Co 2 Si alloy, with an RL min value of -67.61 dB and an EAB of 2.40 GHz. The comprehensive absorption performance of Mn doped Co 2 Si was also improved, and the RL min value of Mn doped with 4 at% was -67.04 dB, and the EAB was 2.39 GHz.This is because that the small Co 2-x M x Si (M=Cu,Mn) alloy can produce multiple reflection and scattering effects, which increase the propagation path of the electromagnetic wave and optimize the impedance matching characteristics of the material.
materials science, multidisciplinary