Atmospheric Corrosion of AZ31B Magnesium Alloy in the Antarctic Low-Temperature Environment

Xi-Zhao Shi,Zhong-Yu Cui,Jie Li,Bing-Chen Hu,Yi-Qiang An,Xin Wang,Hong-Zhi Cui

DOI: https://doi.org/10.1007/s40195-023-01561-4

2023-01-01

Abstract:In this work, the outdoor corrosion behavior of AZ31B magnesium alloy in the Antarctic atmospheric environment was investigated. The surface corrosion state of the specimens exposed to the Antarctic atmosphere for 1 month and 24 months differ significantly. The corrosion rate after 1 month during the summer season was 19.82 g/m 2 ·year and it decreased to 13.87 g/m 2 ·year after two years’ exposure. Corrosion is initiated with pitting corrosion and then evolved to uniform corrosion with prolonging exposure time. The skyward surface exhibited a much severe corrosion than that of the groundward surface, attributed to the long-term existence of the adsorbed electrolyte layer. The corrosion products formed on the alloy exposed in Antarctica environment were MgCO 3 ·3H 2 O, MgCO 3 ·5H 2 O and Mg 2 CO 3 (OH) 2 ·0.5H 2 O, with the MgCO 3 ·3H 2 O as the dominant phase in the initial stage and the Mg 2 CO 3 (OH) 2 ·0.5H 2 O as the dominant phase after long-term exposure.