A General Method to Grow Porous Α‐fe2o3 Nanosheets on Substrates As Integrated Electrodes for Lithium‐Ion Batteries
Linlin Li,Hao Bin Wu,Le Yu,Srinivasan Madhavi,Xiong Wen (David) Lou
DOI: https://doi.org/10.1002/admi.201400050
IF: 5.4
2014-01-01
Advanced Materials Interfaces
Abstract:Up to now, although there have been some reports on the synthesis of α-Fe 2 O 3 nanostructures with enhanced electrochemical properties, the cycling stability and rate capability still remain insuffi cient to fully realize its potential and satisfy the requirements for practical use. Therefore, there is still a great need to identify and realize the most promising structure of α-Fe 2 O 3 that could dramatically improve the battery performance. It is therefore envisioned that advances in LIBs technology can be achieved by combining both integrated electrode design and porous structure with low-dimensional building blocks in a complete electrode confi guration. By virtue of such unique design rationales, the electrochemical activity of electrode materials can be fully manifested because of the absence of ancillary components, fast charge transfer and excellent structural integrity. Although integrated electrodes based on several metal oxides have been reported, facile growth of two-dimensional (2D) α-Fe 2 O 3 nanosheets on various conductive substrates has not been realized to the best of our knowledge, which is possibly associated with the diffi culty to form α-Fe 2 O 3 nanosheets and the surface compatibility issue with the substrates. Herein, we present the rational design and fabrication of α-Fe 2 O 3 nanosheet-based integrated electrodes via a facile and general method. A unique solvothermal approach combined with post-annealing has been developed to grow uniform and well-defi ned porous α-Fe 2 O 3 nanosheets on various metallic substrates. Signifi cantly, the resultant α-Fe 2 O 3 nanosheets possess highly porous texture and small thickness, which are favorable for the fast electrochemical processes and at the same time could effectively accommodate the volume change during cycling. Benefi tting from the hierarchical porous texture constructed by interconnected α-Fe 2 O 3 nanosheets as well as the smart integrated architectures, this integrated binder-free electrode of α-Fe 2 O 3 nanosheets on conductive substrates shows high reversible capacity, enhanced cycling stability and excellent rate capability, indicating their potential application in high-performance LIBs. Porous Fe 2 O 3 nanosheets grown on Ti foil is taken as an example to demonstrate the typical synthesis procedure. After acid treatment to remove the possible oxide/impurity layer on the surface, the Ti foil possesses a fl at and clean surface with no detectable oxide layer (Figure S1, see the Supporting Fabrication of complex nanostructures with controllable morphology, composition, and internal architectures is a promising technology for various applications, such as water splitting, photoelectrochemical devices, and energy conversion and storage. [ 1–4 ] More recently, as an emerging new concept, direct growth of low-dimensional nanostructures (e.g., nanoneedles and nanosheets) on conductive substrates [ 5–7 ] is particularly attractive and has been suggested particularly suitable as integrated electrodes for lithium-ion batteries (LIBs). [ 8–11 ] The constructed architecture is of great signifi cance to provide suffi cient free space and robustness to accommodate the volume variation associated with lithium insertion and extraction, thus dramatically boosting the cycling stability of LIBs. Moreover, each electroactive nanostructure with direct adhesion to the substrate can facilitate charge transport across the electrode, ultimately reducing internal resistance and enhancing the rate performance of LIBs. [ 12–14 ] Therefore, this design rationale holds great potential to achieve superior electrochemical performance for highly reversible and fast lithium storage. Hematite (α-Fe 2 O 3 ) has long been regarded as an appealing anode material for LIBs because of its much higher theoretical capacity (≈1007 mA h g −1 ) than that of commercial used graphite (≈372 mA h g −1 ), as well as nontoxicity and natural abundance. [ 15–17 ] In principle, it is generally believed that the high capacity of α-Fe 2 O 3 derives from the reversible conversion reaction between Li + and α-Fe 2 O 3 , forming Fe nanocrystals dispersed in Li 2 O matrix (Fe x O y + 2 y Li + + 2 y e − ↔ x Fe + y Li 2 O). Despite of these attractive features, α-Fe 2 O 3 suffers from rapid decay in capacity due to the intrinsically drastic volume changes during electrochemical reaction process, and the sluggish reaction kinetics. [ 18,19 ] In order to improve the lithium storage capability, an enormous amount of efforts has been devoted to circumvent above-mentioned problems by designing proper α-Fe 2 O 3 nanostructures, including porous particles, [ 20,21 ]