Abstract:To limit and control the degradation of asphalt pavements and to increase the durability of the asphalt layers, a thorough understanding of the mechanical pavement response is necessary. As a contribution, it is imperative to investigate the fracture behaviours of asphalt mixtures. This paper applies two-dimensional (2D) cohesive zone modeling (CZM) techniques to simulate the microscale crack initiation and propagation within the asphalt mixtures. X-ray computed tomography (X-ray CT) scanning and digital image processing (DIP) techniques were applied to reconstruct the microstructure of asphalt specimens. Finite element (FE) simulations were conducted to simulate the quasi-static indirect tensile test (IDT) with the implementation of a 2D bilinear cohesive zone model. The FE models were optimised and validated based on experimental results. The validated model was then used to investigate the effect of temperature and the air voids on the fracture behaviour of asphalt mixtures. The results show that more significant damage is observed in broader areas outside of the main crack trajectory as the temperature is increased in the range considered in this study (-10 degrees C, 0 degrees C, +10 degrees C). The aggregate-mortar interface exhibited more significant damage than the bulk fracture within the mortar. The deformation voids which are defined as those not crossed by the final crack trajectory have no effect on the maximum reaction force at temperatures above 0 degrees C. Also, deformation voids are found to extend the time to failure. The results contribute to the current research on the fracture behaviour of asphalt mixtures and future investigations are recommended to facilitate the establishment of an asphalt mixture design method and evaluation method based on microscale failure mechanisms. (C) 2019 Elsevier Ltd. All rights reserved.

A Phase-Field Cohesive Zone Model for Fracture Simulation of Asphalt Mixture

A Finite-Volume Implementation of the Phase-Field Model for Brittle Fracture with Adaptive Mesh Refinement

Cohesive Cracking Simulation of Asphalt Mixture with Reflective Crack Through Xfem

Simulation of Low-Temperature Brittle Fracture of Asphalt Mixtures Based on Phase-Field Cohesive Zone Model

Fracture Failure in Crack Interaction of Asphalt Binder by Using A Phase Field Approach

Numerical Simulation of Crack Propagation in Flexible Asphalt Pavements Based on Cohesive Zone Model Developed from Asphalt Mixtures

Fracture Failure of Asphalt Binder in Mixed Mode (modes I and Ii) by Using Phase-Field Model

Numerical Investigation of Asphalt Concrete Fracture Based on Heterogeneous Structure and Cohesive Zone Model

A Phase-Field Framework for Modeling Multiple Cohesive Fracture Behaviors in Laminated Composite Materials

A phase-field cohesive zone model integrated with cell-based smoothed finite element method for quasi-brittle fracture simulations of concrete at mesoscale

Investigation of the Microstructural Fracture Behaviour of Asphalt Mixtures Using the Finite Element Method

A Mesoscale Modelling Approach Coupling SBFEM, Continuous Damage Phase-Field Model and Discrete Cohesive Crack Model for Concrete Fracture

Simulation of Fracture Process of Asphalt Mixture Using Three-Dimension Discrete Element Method

A phase-field model for mixed-mode cohesive fracture in fiber-reinforced composites

Heterogeneous Fracture Simulation of Asphalt Mixture under SCB Test with Cohesive Crack Model

Phase Field Modeling of Mode I Cracking Failure in Asphalt Binder

Modeling Mode I Cracking Failure in Asphalt Binder by Using Nonconserved Phase-Field Model

Three-Dimensional Heterogeneous Fracture Simulation of Asphalt Mixture under Uniaxial Tension with Cohesive Crack Model

Simulation of asphalt concrete cracking using Cohesive Zone Model

A Generalized Phase-Field Cohesive Zone Model (Μpf-Czm) for Fracture

A phase-field regularized cohesive zone model for quasi-brittle materials with spatially varying fracture properties