Studies of Phase Transitions, Raman Spectra and Microwave Dielectric Properties of Perovskite-Structured (na1−xlix)0.5nd0.5tio3 Ceramics

Juncheng Ma,Ying Xiong,Xing Zhang,Zhe Xiong,Bin Tang

DOI: https://doi.org/10.1007/s10854-023-10472-0

2023-01-01

Journal of Materials Science Materials in Electronics

Abstract:High dielectric constant microwave ceramics are essential for ceramic-based devices, such as the dielectric resonator used in miniaturized mobile phone components. Herein, perovskite-type (Na1−xLix)0.5Nd0.5TiO3 (0 ≤ x ≤ 1) ceramics were fabricated using the traditional solid-state processing to explore the changing mechanism of dielectric properties and obtain a component with favorable microwave dielectric properties. The results showed that the maximum εr value (140.3) of samples achieved at x = 0.4 due to changes in bond valence at the B-site, while Q×f and τf values decreased with increasing x value. Raman spectra demonstrated that the broader Raman scattering peaks corresponded to shorter microwave energy propagation decay times, which resulted in a decline of Q×f value. The (Na0.3Li0.7)0.5Nd0.5TiO3 sample showed promising microwave dielectric properties (ɛr = 127.3, Q×f = 2,471 GHz, and τf = − 47.3 ppm/°C). Finally, it was determined that a temperature-stable ceramic with a high εr value could be produced when the x value fell within the range of 0.7 to 0.8.