Abstract:To predict brittle fracture in high-strength steels, this study introduces a methodology for analyzing hydrogen-assisted degradation. The proposed approach considers the fully coupled problems of deformation-hydrogen diffusion and cohesive zone modeling. The analysis of hydrogen diffusion assumes that trapped and lattice hydrogen remain in a equilibrium state while accounting for the relationships between the increase in trap sites and plastic strain. The diffusion model simulates hydrogen diffusion in the small scale yielding (SSY) configuration at a crack tip. The simulation results reveal that hydrogen diffusion follows the hydrostatic stress distribution around the crack tip region. Additionally, the plastic strain near this area leads to an increased number of trap sites. Notably, the simulations indicate that lattice hydrogen is the dominant source of embrittlement when a sufficient amount of hydrogen atoms dissolve into the steel, as compared to trapped hydrogen. The hydrogen-assisted degradation evolution is studied by investigating the influence of hydrogen in a cohesive zone modeling (CZM) with a trapezoidal traction separation law (TSL), based on Hydrogen-Enhanced DEcohesion (HEDE) framework. The fully computational framework is utilized to simulate the hydrogen-charged fracture toughness test in a (CT) specimen made of 30CrMo high strength steel. It is demonstrated that the load bearing capacity of the specimen decreases with an increase in the initial hydrogen concentration. Furthermore, the study examines the evolution of the initial crack time with varying initial hydrogen concentrations. The initial hydrogen concentrations are estimated to match the maximum loads observed in the experimental load-displacement curves based on computational framework. The computational CTOD-R curves for hydrogen generally follow the experimental data, the marginally elevated computational CTOD values to underestimate the embrittling in hydrogen-contaminated steel. Overall, the present study proves the capability of this numerical technique to reproduce experimental findings related to hydrogen-assisted fracture.

Combined Impact of Elastic Stress, Prestrain and Electrochemical Charging on the Hydrogen-Induced Cracking of High-Strength Steel

Numerical Simulation on Hydrogen Induced Cracking Behavior of 4130X Hydrogen Storage Vessel with Defect

Effects of Electrochemical Hydrogen Charging Parameters on the Mechanical Behaviors of High-Strength Steel

Effect of pre-strain on critical conditions for hydrogen-induced delayed cracking and crack nucleation characteristic of DP1180 steel

Effect of Hydrogen Charging on the Stress Corrosion Cracking Behavior of X70 Steel in Simulated Deep Seawater Environment

Effect of hydrogen charging intensities and times on hydrogen embrittlement of Q&P980 steel

Effect of shearing prestrain on the hydrogen embrittlement of 1180 MPa grade martensitic advanced high-strength steel

Effect of Electrochemical Hydrogen Charging on Blistering and Mechanical Properties Behavior of Q690 Steel

Effect of Hydrogen on Plastic Deformation Near Crack-tip of A537 Steel in 3.5%nacl Solution

Analysis of hydrogen-induced delayed cracking and hydrogen trapping behavior in plastically deformed quenching and partitioning steel

Numerical analysis of the fully-coupled continuum cohesive modeling on the hydrogen-assisted degradation behavior in high-strength steel

Effects of hydrogen on the fracture toughness of X80 steel base metal and girth weld under strong cathodic current with in-situ hydrogen charging

Investigation of hydrogen embrittlement behavior in X65 pipeline steel under different hydrogen charging conditions

Experimental and Fractographic Study of the Hydrogen‐Induced Cracking of 45CrNiMoVA Martensitic Advanced High‐Strength Steel

Hydrogen-Assisted Brittle Fracture Behavior of Low Alloy 30CrMo Steel Based on the Combination of Experimental and Numerical Analyses

Hydrogen influence on some advanced high-strength steels

Experimental study on slow tensile, fatigue, and impact on X42 steel and #20 carburizing steel

Influence of hydrogen ingress on residual stress and strain in pipeline steels

Delayed fracture behavior of ultra-high-strength mooring chain steel evaluated by potentiostatic hydrogen-charging combined with SSRT

Comparative evaluation on hydrogen damage behavior of two martensitic high strength press hardening steels

Hydrogen diffusion behavior within microstructures near crack tip: A crystal plasticity study