Abstract:To improve the microstructure of low-temperature-processed CsPbIBr2 films, a chlorobenzene (CB) and isopropyl alcohol (IPA) mixed solution is used as an antisolvent to fabricate CsPbIBr2 films. It is found that the modified film by the mixed antisolvent demonstrates a better morphology, crystallinity, absorption of sunlight, less trap-state density (Ntrap), and suppressed carrier recombination. The modified perovskite solar cells (PSCs) without a hole-transport layer (HTL) achieve a champion efficiency of 7.05%, being much higher by 28.18% than that of the Reference-PSCs without an antisolvent. Moreover, the HTL of undoped zinc phthalocyanine (ZnPc) prepared by solution processing is used to promote charge transfer and protect the CsPbIBr2 film from damage caused by humid air at the CsPbIBr2/carbon interface. The best PSC with a structure of FTO/TiO2/CsPbIBr2/ZnPc/carbon yields a champion efficiency of 8.48% (Reference-PSC, 5.50%) with an open-circuit voltage of 1.23 V. The modified PSCs without encapsulation demonstrate improved humidity stability and retain about 90% (Reference-PSC, ∼70%) of their initial efficiency after storage at a 20% relative humidity in air for 30 days. In addition, the modified PSCs possess good light and thermal stability. Our work provides a feasible low-temperature (150 °C) process to prepare CsPbIBr2 films with the preferred orientation and stable, efficient all-inorganic PSCs (200 °C).The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.1c03554.Photovoltaic parameters, PCE, and J–V curves of the devices treated with the CI antisolvent with different IPA:CB volume ratios; photovoltaic parameters, PCE, and J–V curves of CI-ZnPc-PSCs with different ZnPc concentrations; summary of low-temperature-processed carbon-based all-inorganic CsPbIBr2 PSCs reported in recent years; photographs of color evolution of the Reference-, CI-, IPA-, and CB-films treated at 30 °C for 600 s; thickness of the Reference-film and the CI-film measured by an ellipsometer (PDF)This article has not yet been cited by other publications.

Efficient All-Inorganic CsPbIBr2 Perovskite Solar Cells with an Open Voltage over 1.33 V by Dual-Additive Strategy

A Mixed Antisolvent-Assisted Crystallization Strategy for Efficient All-Inorganic CsPbIBr2 Perovskite Solar Cells by a Low-Temperature Process

Low temperature-processed stable and high-efficiency carbon-based CsPbI2Br perovskite solar cells by additive strategy

A Mixed Antisolvent-Assisted Crystallization Strategy for Efficient All-Inorganic CsPbIBr 2 Perovskite Solar Cells by a Low-Temperature Process

Bifunctional Passivation for Efficient and Stable Low-Temperature Processed All-Inorganic CsPbIBr2 Perovskite Solar Cells

Efficient and Stable All‐Inorganic CsPbIBr 2 Perovskite Solar Cells Enabled by Dynamic Vacuum‐Assisted Low‐Temperature Engineering

Multistrategy Toward Highly Efficient and Stable CsPbI 2 Br Perovskite Solar Cells Based on Dopant‐Free Poly(3‐Hexylthiophene)

Efficient and Stable Carbon‐Based CsPbIBr 2 Perovskite Solar Cells by 4‐Aminomethyltetrahydropyran Acetate Modification

Optimizing the Substrate Pre-Heating and Post-Annealing Temperatures for Fabricating High-Performance Carbon-Based CsPbIBr2 Inorganic Perovskite Solar Cells

Low non-radiative recombination loss in CsPbI<inf>2</inf>Br perovskite solar cells

Secondary Crystallization Strategy for Highly Efficient Inorganic CsPbI2Br Perovskite Solar Cells with Efficiency Approaching 17％

Double Side Interfacial Optimization for Low-Temperature Stable CsPbI 2 Br Perovskite Solar Cells with High Efficiency Beyond 16%

Low non-radiative recombination loss in CsPbI<sub>2</sub>Br perovskite solar cells

Interface Engineering of Low Temperature Processed All-Inorganic CsPbI2Br Perovskite Solar Cells Toward PCE Exceeding 14%

Vapor-assisted deposition of CsPbIBr2 films for highly efficient and stable carbon-based planar perovskite solar cells with superior Voc

Hierarchically Manipulated Charge Recombination for Mitigating Energy Loss in CsPbI 2 Br Solar Cells

n-type absorber by Cd2+ doping achieves high-performance carbon-based CsPbIBr2 perovskite solar cells

High‐Efficiency Carbon‐based CsPbI2Br Perovskite Solar Cells from Dual Direction Thermal Diffusion Treatment with Cadmium Halides

High-performance carbon-based CsPbI2Br perovskite solar cells via small molecule modification

High‐Efficiency Carbon‐Based CsPbIBr 2 Solar Cells with Interfacial Energy Loss Suppressed by a Thin Bulk‐Heterojunction Layer

Low‐Temperature Crystallization of CsPbIBr 2 Perovskite for High Performance Solar Cells