Abstract:Cracking of pavement materials affects the service performance of pavement structures. It is widely investigated by discrete element method (DEM) because the DEM can present the cracking behavior and mechanism from the mecroscopic perspective. However, improper calibration method is time-consuming and the simulation results are not applicable for different loading conditions. To address this issue, a systematical calibration method is proposed to establish a more reasonable DEM model, and it is used to explore the cracking behavior and mechanism for pavement materials. The fiber reinforced cement treated aggregates (F-CTA) used to construct the pavement base are selected as an example to elaborate the process. First, contacts within the F-CTA were divided into five groups according to physical components. Then, laboratory tests were performed to obtain macro mechanical properties including strength and modulus. Next, the corresponding virtual tests were established and the contact model parameters were calibrated from mono-component to mixture. This calibration method was validated by the three-point bending test incorporating all contact parameters obtained from the above calibrations and the process of cracking evolution was analyzed. Results show that the simulated mechanical responses and crack distribution based on the systematical calibration are in good agreement with laboratory measurements and observations, exhibiting well reliability for calibrating contact parameters of composite material. Young's modulus of the F-CTA is sensitive to the mecro effective modulus in the virtual indirect tensile test while Young's modulus and tensile strength are vulnerable to the mecro cohesion in the virtual uniaxial compression test. The mortar-aggregate and mortar-aggregate interface is relatively weak where cracks are prone to appear. The fibers can optimize the distribution of the crack network. The cracking evolution contains three stages and the second stage has a significant influence on the cracking behavior of the F-CTA.

Characteristic Analysis of Cement Grouted Asphalt Mixture Cracking Based on Acoustic Emission

Diagnosis of Damage Evolution Process for Asphalt Mixtures Using Pattern Recognition with Acoustic Emission Signals

Systematical Calibration and Validation of Discrete Element Models for Fiber Reinforced Cement Treated Aggregates

Characteristics of Undamaged Asphalt Mixtures in Tension and Compression

Wavelet and Fractal Analysis of Acoustic Emission Characteristic of Fatigue Damage of Asphalt Mixtures

Crack Initiation in Asphalt Mixtures under External Compressive Loads

Cracking Process Analysis and Fracture Pattern Recognition of Asphalt Mixture Based on Acoustic Emission Characteristics

Evaluation Approach of Fracture Behavior for Asphalt Concrete with Different Aggregate Gradations and Testing Temperatures Using Acoustic Emission Monitoring

Damage Evolution Analysis in Cementitious Mixtures Using Acoustic Emission Techniques

Multiscale Study of the Effect of Fly Ash Geopolymer on the Fatigue Cracking of Cement Stabilized Macadam

In-situ Acoustic Emission Investigation of Asphalt Fracture Process and Damage Quantification for Different Asphalt Mixtures

Acoustic Emission Characterization of the Fracture Process in Fly Ash Fiber–Reinforced Asphalt Concrete

Influences of an Artificial Three-Dimensional Cementitious Network on the Fracture Property of Cement Casting Asphalt Mixture

Micro-Scale Fracture Characteristics of Emulsified Asphalt Cold Recycled Mixture Based on Discrete Element Method

Damage Analysis of Semi-Flexible Pavement Material under Axial Compression Test Based on Acoustic Emission Technique

Damage Evolution in Asphalt Mixtures Based on In-Situ CT Scanning

Damage Fracture Characterization of Asphalt Mixtures Considering Freeze-Thaw Cycling and Aging Effects Based on Acoustic Emission Monitoring

Characterization of crack resistance mechanism of fiber modified emulsified asphalt cold recycling mixture based on acoustic emission parameters

Internal Crack Growth of Asphalt Binders During Shear Fatigue Process

Temperature dependency analysis of the fracture characteristics of semi-flexible pavement (SFP) mixtures using acoustic emission technique

Study on Mechanics-Based Cracking Resistance of Semiflexible Pavement Materials