9,10-Anthraquinone/K 2 CuFe(CN) 6 : A Highly Compatible Aqueous Aluminum-Ion Full-Battery Configuration
Lijing Yan,Xiaomin Zeng,Shu Zhao,Wei Jiang,Zeheng Li,Xuehui Gao,Tiefeng Liu,Zekai Ji,Tingli Ma,Min Ling,Chengdu Liang
DOI: https://doi.org/10.1021/acsami.0c20543
2021-02-09
Abstract:Temporally intermittent and spatially dispersed renewable energy sources strongly call for large-scale energy storage devices. Aqueous aluminum-ion batteries show great potential for application due to their safety and low cost. Thus far, however, the ideal full-battery configuration is beyond the scope due to shortcomings with regards to suitable anode and cathode materials. Herein, we report a pioneering aqueous aluminum-ion battery system consisting of a Prussian white cathode, 1 M Al<sub>2</sub>(SO<sub>4</sub>)<sub>3</sub> aqueous electrolyte, and an organic 9,10-anthraquinone anode. The oxidation capability of the Prussian white cathode during the first charging allows for the fabrication of the full battery without pre-inserting aluminum ions, thus making the rocking-chair-type battery feasible. Importantly, the open-framework structure of the Prussian white and distinct enolization charge storage mechanism of 9,10-anthraquinone ensure fast reaction kinetics. The full battery exhibits cycling stability with a capacity retention of 89.1% over 100 cycles at 500 mA g<sup>–1</sup>, finishing a cycle in about 10 min. This work provides a pathway for developing rechargeable aqueous aluminum-ion batteries.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c20543?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c20543</a>.TGA curve, HRTEM, EDS mapping, XPS spectra, and ICP-OES results of the as-prepared K<sub>2</sub>CuFe(CN)<sub>6</sub>, monoclinic molecular structure of AQ, XRD patterns and <sup>1</sup>H NMR spectra of ball-milled raw AQ and AQ/C, XRD patterns and SEM images of the AQ electrode before and after reduction, CV curves of K<sub>2</sub>CuFe(CN)<sub>6</sub> in 0.5 M K<sub>2</sub>SO<sub>4</sub>, the discharge–charge curves of AQ and K<sub>2</sub>CuFe(CN)<sub>6</sub> in the 100th, 300th, and 500th cycle, the electrochemical performance of carbon black, EDX characterization of the K<sub>2</sub>CuFe(CN)<sub>6</sub> electrode at different states, the electrochemical performance of AQ, K<sub>2</sub>CuFe(CN)<sub>6</sub>, and full battery in the 0.1 M K<sub>2</sub>SO<sub>4</sub> + 0.5 M Al<sub>2</sub>(SO<sub>4</sub>)<sub>3</sub> (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c20543/suppl_file/am0c20543_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology