Damage Characteristics of Steel Fiber-reinforced Concrete Based on Direct Tensile Test

ZHANG Dong-mei,ZHANG Xin

DOI: https://doi.org/10.19721/j.cnki.1001-7372.2023.04.013

2023-01-01

Abstract:The coupling effects of the content, length, and type of fiber on the cracking mode, tensile strength, peak strain, and post-cracking ductility were studied using direct tensile tests of steel fiber-reinforced concrete（SFRC） and DIC technology. The experimental results showed that the cracking sound, crack shape, and number of cracks in SFRC under direct tension were significantly affected by the content of steel fiber. The tensile strength, peak strain, and post-cracking ductility all increased after adding steel fiber to the concrete. Compared with milled steel fibers, which tend to form agglomerates during pouring, hooked steel fibers are easier to pour uniformly and densely with the concrete matrix, and the resistance of the end hook greatly improves the bridging effect. Thus, the hooked steel fibers have a superior performance in improving the tensile strength and post-cracking ductility. The mesoscale failure mechanism of SFRC under direct tension was further revealed. The mesoscale failure of SFRC occurred in four stages. Stage Ⅰ was the elastic stage; stage Ⅱ involved mesoscale crack propagation; stage Ⅲ was mesoscale crack failure; and stage Ⅳ included the pulling-out of the fibers. Consequently, a stress-strain model of SFRC was proposed that considered the coupling effects of the concrete matrix characteristics, fiber volume content, fiber length, and fiber type. Based on this model, a tensile damage factor was introduced to quantitatively investigate the effects of the tensile strength, peak strain, and post-cracking ductility on the damage development characteristics of SFRC.