Synthesis of magnetic biochar-supported Fe-Cu bimetallic catalyst from pulp and paper mill wastes for the Fenton-like removal of rhodamine B dye
Yuehao Shen,Yuxin Xiao,Hongjie Zhang,Hongjie Fan,Yao Li,Zhongli Yan,Wen-Hui Zhang,ZhongLi Yan
DOI: https://doi.org/10.1016/j.cej.2023.146823
IF: 15.1
2023-11-02
Chemical Engineering Journal
Abstract:Treating the wastes generated from pulp and paper mills, such as black liquor and Fenton sludge is challenging. In this study, the biochar-supported Fe-Cu bimetallic catalysts were synthesized by a one-step pyrolysis method using Fenton sludge as iron source, acid-precipitated black liquor (APBL) as carbon source and copper nitrate as copper source. The catalysts were used to remove rhodamine B (RhB) dye from aqueous solution by Fenton-like reaction. The optimal catalyst (FeCu@BC 600-2 ) was pyrolyzed at 600 °C with an Fe/Cu mixing ratio of 2 and consisted of mesoporous biochar supported nanoscale Fe 3 O 4 and Cu 0 . It had a specific surface area of 104.6 m 2 ·g −1 and a saturation magnetization of 33.3 emu·g −1 . In the FeCu@BC 600-2 /H 2 O 2 system, RhB dye (10 mg·L -1 ) was completely removed within 60 min at acidic pH (initial pH 3, 0.2 g·L -1 catalyst, 1 mM H 2 O 2 ) or 6 h at neutral pH (initial pH 7, 0.25 g·L -1 catalyst, 25 mM H 2 O 2 ) at 30 °C. Moreover, the FeCu@BC 600-2 exhibited good magnetic separation ability, low metal leaching, excellent reusability and broad applicability to other synthetic dyes. The dye removal mechanism involved the synergistic effect of adsorption and catalytic oxidation (especially heterogeneous catalytic oxidation). At acidic pH, RhB degradation was due to •OH radical, which was generated from the activation of H 2 O 2 by ≡Cu(I) or Cu(I) oxidized from Cu 0 and ≡Fe(II) in Fe 3 O 4 . At neutral pH, RhB degradation was mainly due to •OH and 1 O 2 with the former being produced by ≡Cu(I) and ≡Fe(II). Furthermore, Cu(I) oxidized from Cu 0 and the active functional groups (such as sp 2 C = C) in the biochar facilitated the reduction of Fe(III) to Fe(II), resulting in a high catalytic oxidation efficiency.
engineering, chemical, environmental