Preparation and evaluation of GCD-1 lunar regolith simulant based geopolymer activated by solid sodium silicate
Shuo Li,Zihan Zhou,Guo Hu,Jun Wu
DOI: https://doi.org/10.1016/j.cscm.2024.e03273
IF: 4.934
2024-05-18
Case Studies in Construction Materials
Abstract:In this study, a new lunar regolith simulant, named "GCD-1", was formulated by combining various minerals, such as anorthite, albite, pyroxene, ilmenite, slag, and fly ash. Through X-ray fluorescence spectroscopy (XRF) and X-ray diffraction (XRD) analysis, it was verified that the main mineral composition of GCD-1 was basically the same as that of the lunar soil at the Apollo 14 landing site, in which the deviation in the main compound (i.e., SiO 2 and Al 2 O 3 ) was within 0.5%. Furthermore, GCD-1 based geopolymer was prepared by the one-part method, which was a mixture of solid GCD-1 precursor, solid sodium silicate (SS) activator, and water. The average daytime temperature at the lunar equator, which was calculated to be 60°C, was set as the curing temperature for the GCD-1 based geopolymer. The strength development of the GCD-1 based geopolymer was then characterized by unconfined compressive strength (UCS) for 3, 7, and 12 curing days to consider the effectiveness of the factors (solid SS to lunar regolith simulant [S/L] and water to binder ratio [W/B]). The micro-analysis tests including scanning electron microscope-energy dispersive spectrometer (SEM-EDS), mercury intrusion porosimetry (MIP), and brunner-emmet-teller (BET), were further conducted to investigate the microstructural development of the GCD-1 based geopolymer. Results showed that the increase of the W/B ratio in the GCD-1 based geopolymer tended to increase the total porosity of the sample, thereby inducing a lower UCS. At the same time, for a fixed W/B ratio, the higher S/L ratio had a certain inhibition effect on the hydration reaction, which caused the reduction in the UCS of the sample. The highest UCS of the GCD-1 based geopolymer reaching 30.54 MPa, was achieved under the simulated lunar equatorial daytime temperature for 12 days with W/B and S/L ratios set at 0.25 and 0.18, respectively. Microstructure and mineralogy analyses indicated that the hydrated sodium aluminosilicate (N-A-S-H) gels contributed to reducing the sample's porosity, thereby enhancing the UCS. The relationship between the UCS and total porosity of GCD-1 based geopolymer was then derived. The results of the current study are crucial for lunar base construction with in-situ resources.
materials science, multidisciplinary,engineering, civil,construction & building technology