Abstract:Titanium and titanium alloy materials are often made as medical implants. Surface properties of titanium medical implants play decisive roles for antibacterial and biological response and tissue biocompatibility. In this study, cathode arc evaporation (CAE) technology was used to deposit TiNb–Zr–Ta and nitrogen-doped TiNb–Zr–Ta coatings with nanostructures on the Ti–6Al–4V dental abutment screws. The deposited coatings were then oxidized at high temperature to produce different oxides on the surface of the coatings. The mechanical properties , antibacterial properties and biocompatibilities of the coatings were analyzed. The effect of coatings on the abutment screw loosening and removal torque between the abutment screw and the pure titanium implant fixture was studied by removal torque measurement. In addition, Staphylococcus aureus (S. aureus) was used for evaluating the antibacterial properties of coatings, and mouse fibroblasts (L929) were used for ISO 10993-5 cytotoxicity analyses to determine whether it had good biocompatibility. Nanolayered structures and multiphases of polycrystalline TiNb–Zr–Ta were obtained by co-deposition of Ta , Zr and TiNb. When small content of N was introduced, the TiNb–Zr–Ta(N) showed a polycrystalline TiNb–Zr–Ta where N atoms entered the metallic lattice at interstitial sites. After oxidation, oxide phases of Ta 2 O 5 , TiO 2 , Nb 2 O 5 and ZrO 2 were formed on the surface of TiNb–Zr–Ta and TiNb–Zr–Ta(N). Ta 2 O 5 was obtained on the surface of the coating prior to other oxides such as TiO 2 , Nb 2 O 5 and ZrO 2 . The deposited TiNb–Zr–Ta and TiNb–Zr–Ta(N) coatings had high contact angle and exhibited a hydrophobic feature, while the annealed TiNb–Zr–Ta–O and TiNb–Zr–Ta(N)–O showed hydrophilicity. The deposited TiNb–Zr–Ta had similar hardness and Young's modulus values to that of the uncoated Ti–6Al–4V. When N was doped, the TiNb–Zr–Ta(N) had the highest hardness and Young's modulus. The hardness of the annealed TiNb–Zr–Ta(N) coating only decreased slightly due to the small oxide layer of ∼140 nm. Compared with the uncoated Ti–6Al–4V, TiNb–Zr–Ta serial coatings deposited on abutment screws had higher removal torques, which prevented the abutment screw of dental implant from loosening after long-term use. The biocompatibility of TiNb–Zr–Ta serial coatings was similar to that of the uncoated Ti–6Al–4V. In addition, the oxidized TiNb–Zr–Ta and TiNb–Zr–Ta(N) coatings had excellent antibacterial properties. It is speculated that the resulting Ta 2 O 5 of both coatings may inhibit bacterial growth and improve the antibacterial effect. Based on the above advantages, the TiNb–Zr–Ta serial coatings are expected to have the potential to be applied to biomedical implants.

A Novel Biomedical TiN-embedded TiO2 Nanotubes Composite Coating with Remarkable Mechanical Properties, Corrosion, Tribocorrosion Resistance, and Antibacterial Activity

A novel biomedical TiN-embedded TiO 2 nanotubes composite coating with remarkable mechanical properties, corrosion, tribocorrosion resistance, and antibacterial activity

Enhanced Wear Resistance, Antibacterial Performance, and Biocompatibility Using Nanotubes Containing Nano-Ag and Bioceramics in Vitro

Mechanical, biocorrosion, and antibacterial properties of nanocrystalline TiN coating for orthopedic applications

Mechanical, antibacterial and cytotoxic characteristics of nanolayered TiNb–Zr–Ta and nitrogen-doped TiNb–Zr–Ta coatings

Tantalum Nitride-Decorated Titanium with Enhanced Resistance to Microbiologically Induced Corrosion and Mechanical Property for Dental Application

In-situ construction of the nanostructured TiO 2 /TiN composite films by induction heat treatment: Improved mechanical, corrosion, and biological properties

In Vitro Corrosion and Tribological Behavior of Multiwall Carbon Nanotube-Coated Ti-6Al-4V/Tantalum Carbide Surface for Implant Applications

Silk Fibroin/ZnO Coated TiO2 Nanotubes for Improved Antimicrobial Effect of Ti Dental Implants

Electrochemical deposition multi-walled carbon nanotube coatings on the surface of Ti6Al4V alloy for enhancing its biotribological properties

Mechanical and Corrosion Resistance Properties of Tio2 Nanoparticles Reinforced Ni Coating by Electrodeposition

A Prospective Material for Orthopedic Applications: Ti Substrates Coated with a Composite Coating of a Titania-Nanotubes Layer and a Silver-Manganese-doped Hydroxyapatite Layer

Surface Modification and Tribological Performance of Calcium Phosphate Coatings with TiO2 Nanoparticles on VT1-0 Titanium by Micro-Arc Oxidation

Simultaneously Improved Bio-Tribological and Biological Corrosion Properties of Tac Film Coated on Ti6Al4V by Sealing with ALD

Preparation and Biocompatibility of Corrosion-Resistant Micro-Nano Bipolar Structures on the Surface of TC4 Titanium Dental Implants

Morphology and Structure of TiO2 Nanotube/Carbon Nanostructure Coatings on Titanium Surfaces for Potential Biomedical Application

Enhanced Corrosion Resistance and Local Therapy from Nano-Engineered Titanium Dental Implants

Covalent Grafting of Tanfloc on Titania Nanotube Arrays: An Approach to Mitigate Bacterial Adhesion and Improve the Antibacterial Efficacy of Titanium Implants

Corrosion, Oxidation and High-Temperature Tribological Properties of Ti–B–N Coatings

In vitro corrosion behavior of coated Ti6Al4V with TiO2, ZrO2, and TiO2/ZrO2 mixed nanofilms using atomic layer deposition for dental implants

Tin Coated Stainless Steel Bracket: Tribological, Corrosion Resistance, Biocompatibility and Mechanical Performance