Abstract:Cost-effective and environmentally friendly sorbents were created for capturing CO 2 by incorporating monoethanolamine (MEA) and tetraethylenepentamine (TEPA) onto a microporous activated carbon (AC) material. The application of a KOH reagent enhanced the surface area and pore volume of the carbon material. The BET, SEM, EDX, and FTIR techniques were employed to analyze the structural and surface properties of the developed samples. Raw AC possessed the highest surface area and largest micropore volume equal to 786 m 2 /g and 0.33 cm 3 /g, respectively. The amine impregnation increased the nitrogen content of the carbon material, but it also significantly reduced the BET surface area and total pore volume, which are primarily responsible for physically adsorbing CO 2 towards ACs. The CO 2 adsorption performance of the raw and impregnated ACs was experimentally evaluated using thermogravimetric analysis (TGA) at different adsorption temperatures (25 and 50 °C) and CO 2 concentrations (10 and 90 vol.%). The findings demonstrated that the raw AC exhibited the highest capacity for CO 2 adsorption. Specifically, at a temperature of 25 °C and pressure of 1 bar (10 vol.% CO 2 , N 2 balance), the raw AC achieved an uptake of 1.2 mmol/g, which was 60.3% and 79.3% higher compared to the CO 2 uptake of MEA-AC (0.5 mmol/g) and TEPA-AC (0.3 mmol/g), respectively. It is surprising that the combined uptake of CO 2 + H 2 O increased by 12.5 and 23.4 wt.% (equivalent to 7 and 13 mmol/g) for MEA-AC and TEPA-AC, respectively, when humid flue gas was taken into account under the conditions of 50 °C, with 10 vol.% CO 2 , 4 vol.% H 2 O, and N 2 balance. These results indicate that the presence of H 2 O facilitates the chemisorption of CO 2 by the novel and highly promising carbon-based sorbent prepared in this study, leading to an increased capacity for adsorbing CO 2 under water vapor containing flue gases.

Hydrophobic functionalized amine-impregnated resin for CO2 capture in humid air

Polyethylenimine-Grafted Hkust-Type Mof/Poiyhipe Porous Composites (Pei@Pgd-H) As Highly Efficient Co(2 )Adsorbents

Preparation and Co2 Sorption/Desorption of N-(3-Aminopropyl) Aminoethyl Tributylphosphonium Amino Acid Salt Ionic Liquids Supported into Porous Silica Particles

Porosity and Hydrophilicity Modulated Quaternary Ammonium-Based Sorbents for CO2 Capture

Cost-effective carbon-based amine adsorbents for carbon capture: Equilibrium, kinetics and selectivity

Zeolite@Mesoporous silica-supported-amine hybrids for the capture of CO 2 in the presence of water

Carbon dioxide capture by functionalized solid amine sorbents with simulated flue gas conditions.

Study on CO2 capture in humid flue gas using amine-modified ZIF-8

Direct Air Capture of CO2 Using Bi-Amines-functionlized Hierarchical Mesoporous Silica: Effects of Organic Amine Loading, Moisture and Temperature

Polyethylenimine-impregnated resin for high CO2 adsorption: an efficient adsorbent for CO2 capture from simulated flue gas and ambient air.

Impregnation of Polyethylenimine in Mesoporous Multilamellar Silica Vesicles for Co2 Capture: A Kinetic Study

Facile fabrication of mesoporosity silica as support for solid amine CO2 adsorbents with enhanced adsorption capacity and kinetics

CO2 Absorption over Ion Exchange Resins: the Effect of Amine Functional Groups and Microporous Structures

Application of Polyethylenimine‐impregnated Solid Adsorbents for Direct Capture of Low‐concentration CO2

The effect of humidity on the enhanced CO2 adsorption of amine-functionalized microporous activated carbon

Direct air capture of CO2 by amine-impregnated resin: The effect of resin pore structure and humid conditions

Surfactant promoted solid amine sorbents for CO 2 capture

Adsorption of H2o and Co2 on Supported Amine Sorbents

Amine-Functionalized Quasi-MOF for Direct Air Capture of CO<sub>2</sub>

Continuous CO2 Capture in Dual Fluidized Beds Using Silica Supported Amine

Development and characterization of amine-functionalized hyper-cross-linked resin for CO2 capture