Combination of Chemical Activation and Nitrogen Doping Toward Hierarchical Porous Carbon from Houttuynia Cordata for Supercapacitors

Weiwei Zhu,Dekui Shen,Haijiao Xie
DOI: https://doi.org/10.1016/j.est.2022.106595
IF: 9.4
2023-01-01
Journal of Energy Storage
Abstract:Nitrogen-doped hierarchical porous carbon (N-HPC) was prepared from houttuynia cordata under the combined action of chemical activation and nitrogen-doping. The etching behavior of activator was enhanced by nitrogen doping while the proportion of pyridinic and pyrrolic nitrogen was promoted by the etching behavior. Theo-retical calculations reveal that the activator is more likely to adsorb on the nitrogen-doped carbon surface and tend to etch carbon atoms besides the pyridinic, graphitic nitrogen and pyridine-N-oxide. The prepared N-HPC displays a large specific surface area of 2491.5 m2 g-1, and the nitrogen atoms in N-HPC exist mainly in the form of pyridinic and pyrrolic nitrogen. The N-HPC electrode exhibits a high specific capacitance of 220.5 F g-1 at 0.5 A g-1 and good rate characteristic in 6 M KOH electrolyte. The assembled symmetric supercapacitors exhibit a high energy density of 9.82 W h kg-1 at a power density of 162.33 W kg-1. This work reveals the interaction between nitrogen-doping process and etching behavior of the activator, and proposes a novel route for the synthesis of biomass-based carbon material for supercapacitors.
What problem does this paper attempt to address?