Abstract:Nowadays the development of high-field magnets strongly relies on the performance of superconducting materials. Iron-based superconductors exhibit high upper critical fields and low electromagnetic anisotropy, making them particularly attractive for high-field applications, especially in particle accelerator magnets, nuclear magnetic resonance spectrometers, medical magnetic resonance imaging systems and nuclear fusion reactors. Herein, through an industrially scalable and cost-effective manufacturing strategy, a practical level critical current density up to 1.1x10^5 A/cm2 at 4.2 K in an external magnetic field of 10 T was achieved in Cu/Ag composite sheathed Ba0.6K0.4Fe2As2 superconducting tapes. The preparation strategy combines flat rolling to induce grain texture and a subsequent hot-isostatic-pressing densification. By varying the parameters of rolling, the degree of grain texture was engineered. It is found that the transport properties of the Ba1-xKxFe2As2 tapes can be enhanced by applying a large amount of deformation during rolling, which can be attributed to the improved degree of c-axis texture. Microstructure characterizations on the highest-performance tape demonstrate that the Ba1-xKxFe2As2 phase has a uniform element distribution and small grains with good connectivity. Grain boundary pinning is consequently enhanced as proved by large currents circulating through the sample even at 25 K. Our work proves that Cu/Ag composite sheathed Ba1-xKxFe2As2 superconducting tapes can be a promising competitor for practical high-field applications in terms of the viable, scalable and cost-effective fabrication strategy applied and the high transport properties achieved in this work.

Constitutive Behaviour Study of Ba X K1− X Fe2As2 Iron-Based Superconducting Powder

Experimental Investigation on Constitutive Behaviour of Superconducting Powder BSCCO

Role of heat and mechanical treatments in the fabrication of superconducting Ba0.6K0.4Fe2As2 ex-situ Powder-In-Tube tapes

Origin and elimination of excess iron particles in off-stoichiometric Ba0.6K0.5-βFe2As2+δ superconductors

Critical Current Degradation Behavior of 7-Filamentary Ba1−x K X Fe2As2 Tapes under Uniaxial Strain

Numerical Modelling of Bscco Powder Deformation in the Bi-2223/Ag Tape Rolling Process

High-performance Ba1-xKxFe2As2 superconducting tapes with grain texture engineered via a scalable and cost-effective fabrication

Influence of Precursor Powder Fabrication Methods on the Superconducting Properties of Bi-2223 Tapes

Density dependent constitutive model for Bi-2212 powder compression deformation

Textured Sr1-xKxFe2As 2 superconducting tapes with high critical current density

Observation of reversible critical current performance under large compressive strain in Sr0.6K0.4Fe2As2 tapes

Critical current density and microstructure of iron sheathed multifilamentary Sr1-xKxFe2As2/Ag composite conductors

Influences of Pb content on the critical current of Bi-2223 multi-filamentary tapes

High-performance Ba1-xKxFe2As2 superconducting joints for persistent current operation

Iron-Based Superconductors for High-Field Applications: Realization of High Engineering Critical Current Density

Fabrication of Multifilamentary Powder in Tube Superconducting Tapes of Bi-2223 with Sr Deficient Starting Composition

Mechanochemical synthesis of pnictide compounds and superconducting Ba0.6K0.4Fe2As2 bulks with high critical current density

Tailoring the Critical Current Properties in Cu-sheathed Sr1−xKxFe2As2superconducting Tapes

Finite Element Analysis of the Effect of Semi-Die Angle During Drawing on the Properties of Bi-2223 Superconducting Wires

Compressive, Tensile, And Dynamic Behavior Of Nanophase Iron

Strongly enhanced current densities in Sr0.6K0.4Fe2As2 superconducting tapes