Abstract:A type of novel copper-based catalysts supported on MIL-125(Ti), a kind of metal–organic frameworks (MOFs), noted as Cu-MIL-125(Ti), was synthesized for the selective catalytic reduction (SCR) of NO with CO. The reactivity of Cu-MIL-125 catalysts for selective catalytic reduction of NO by CO (SCR-CO) was evaluated in a fixed bed reactor. A number of characterization techniques were used to explore the basic physical–chemical properties and the reaction mechanism. The results showed that the large specific surface area and micro-mesopores of the MIL-125 carrier promoted the high dispersion of Cu species, leading to the outstanding SCR-CO performance. Among the results, 90 % NO conversion and 92 % N 2 selectivity were proved for the 6.2Cu-MIL-125 catalyst at 325 °C in oxygen-rich environment. XRD results showed that the metal organic frame structure and TiO 2 structure coexisted in the catalysts, which was the major factor to influence the NO reduction efficiency. XPS characterization and H 2 -TPR reduction results showed that the catalytic performance of the catalyst was mainly determined by the path of Cu 2+ reduction to Cu + and then Cu + to Cu 0 . Lewis acid on the catalyst surface played an important role in the CO-SCR reaction. In situ DRIFTS study proved that NO was first adsorbed on the surface of the catalyst to form different nitrate, NCO and isocyanate species. Then the adsorbed NO and the intermediates reacted with gaseous CO, which is a typical interaction between adsorbed molecules and gas molecules. Oxygen vacancies on the catalyst surface was involved in the reaction of CO to CO 2 . The whole reaction follows the M–K mechanism and the E-R mechanism. A preliminary reaction pathway was proposed based on the in situ DRIFTS results.

Monolithic CuMnO2-Nanosheet-Based Catalysts in Situ Grown on Stainless Steel Mesh for Selective Catalytic Reduction of NO with CO

Monolithic CuMnO 2 -Nanosheet-Based Catalysts In Situ Grown on Stainless Steel Mesh for Selective Catalytic Reduction of NO with CO

Flexible Ti Mesh-Supported MnO x –CuO x /TiO 2 Nanosheet Monolithic Catalysts for Low-Temperature Selective Catalytic Reduction of NO x with NH 3

Flexible monolithic Pt/CuO-Fe2O3/TiO2 catalysts integrated on Ti mesh for efficient NO removal via CO-SCR reaction

Recent Advances of Cu-Based Catalysts for NO Reduction by CO under O2-Containing Conditions

Mn-Based Catalysts in the Selective Reduction of NOx with CO: Current Status, Existing Challenges, and Future Perspectives

Surface Tailoring on Bifunctional CuOx/MnO2 Catalyst to Promote the Selective Catalytic Reduction of NO with NH3 and Oxidation of CO with O2

Novel Homogeneous and Mesoporous MnOx-Doped Ceria Nanosheets As Catalysts for Low-Temperature Selective Catalytic Reduction

Recent advances in NO reduction with CO over copper-based catalysts: reaction mechanisms, optimization strategies, and anti-inactivation measures

Spinel Structured CoaMnbOx Mixed Oxide Catalyst for the Selective Catalytic Reduction of NOx with NH3

Bifunctional Catalyst of CuMn-HZSM-5 for Selective Catalytic Reduction of NO and CO Oxidation under Oxygen Atmosphere

Selective catalytic reduction of nitric oxide with carbon monoxide over alumina-pellet-supported catalysts in the presence of excess oxygen

Copper-based catalysts supported on novel Metal-Organic Framework MIL-125(Ti) for selective catalytic reduction of NO with CO

Three-Dimensional Spherical CuCoAlO<sub>X</sub> Catalyst with a Micro-/ Nanoporous Structure for Low-Temperature CO-SCR Denitration

Three-Dimensional Spherical CuCoAlO<sub><i>x</i></sub> Catalyst with a Micro-/Nanoporous Structure for Low-Temperature CO-SCR Denitration

Subnanometric Pt on Cu Nanoparticles Confined in Y‐zeolite: Highly‐efficient Catalysts for Selective Catalytic Reduction of NO x by CO

The catalytic mechanisms and design strategies of noble metal catalysts for selective reduction of NOx with CO

Transition metal-based catalysts for selective catalytic reduction of NO by CO: A state-of-the-art review

Manganese Oxide Catalysts Supported on Zinc Oxide Nanorod Arrays: A New Composite for Selective Catalytic Reduction of NOx with NH3 at Low Temperature

Freestanding Cobalt‐Aluminum Oxides on USY Zeolite As an Efficient Catalyst for Selective Catalytic Reduction of NOx

MnyCo3−yOx Bimetallic Oxide Prepared by Ultrasonic Technology for Significantly Improved Catalytic Performance in the Reduction of NOx with NH3