Abstract:Electrochemical CO2 reduction is a promising strategy for the utilization of CO2 and intermittent excess electricity. Cu is the only single metal catalyst that can electrochemically convert CO2 into multicarbon products. However, Cu exhibits an unfavorable activity and selectivity for the generation of C2 products because of the insufficient amount of CO* provided for the C-C coupling. Based on the strong CO2 adsorption and ultrafast reaction kinetics of CO* formation on Pd, an intimate CuPd(100) interface was designed to lower the intermediate reaction barriers and improve the efficiency of C2 product formation. Density functional theory (DFT) calculations showed that the CuPd(100) interface enhanced the CO2 adsorption and decreased the CO2* hydrogenation energy barrier, which was beneficial for the C-C coupling. The potential-determining step (PDS) barrier of CO2 to C2 products on the CuPd(100) interface was 0.61 eV, which was lower than that on Cu(100) (0.72 eV). Encouraged by the DFT calculation results, the CuPd(100) interface catalyst was prepared by a facile chemical solution method and characterized by transmission electron microscopy. CO2 temperature-programmed desorption and gas sensor experiments further confirmed the enhancement of the CO2 adsorption and CO2* hydrogenation ability of the CuPd(100) interface catalyst. Specifically, the obtained CuPd(100) interface catalyst exhibited a C2 Faradaic efficiency of 50.3% ± 1.2% at −1.4 VRHE in 0.1 M KHCO3, which was 2.1 times higher than that of the Cu catalyst (23.6% ± 1.5%). This study provides the basis for the rational design of Cu-based electrocatalysts for the generation of multicarbon products by fine-tuning the intermediate reaction barriers.A CuPd(100) catalyst was designed and fabricated to improve the selectivity of the electroreduction of CO2 to C2 products by tuning the CO2 adsorption ability and intermediate reaction barriers.

Comparative computational study of CO2 hydrogenation and dissociation on metal-doped Pd clusters

Density Functional Theory Study of CO2 Hydrogenation on Transition-Metal-Doped Cu(211) Surfaces

Theoretical Investigation on the CO2 Hydrogenation to Methanol Mechanism at Electron-Rich Active Interface over Cu/Ga-Ti-Al-O Catalyst

Comparative computational study of CO2 dissociation and hydrogenation over Fe-M (M = Pd, Ni, Co) bimetallic catalysts: The effect of surface metal content

Computational Investigation of Fe–Cu Bimetallic Catalysts for CO2 Hydrogenation

Mechanistic Study Of Pd-Cu Bimetallic Catalysts For Methanol Synthesis From Co2 Hydrogenation

CuPd Bimetallic Catalyst with High Cu/Pd Ratio and Its Application in CO2 Hydrogenation

Theoretical Investigation of the Properties of Pd2Cu Intermetallics and CO2 Hydrogenation to Ethanol Catalyzed on Pd2Cu (110)

Carbon Monoxide Promotes the Catalytic Hydrogenation on Metal Cluster Catalysts

Tunable Pd enrichment for switching CO2 electroreduction product selectivity from HCOOH to CO

Hydrogen Activation and Its Role in Co2 Hydrogenation on Isolated Pd Species of Cupd0.1/Γ-Al2o3: the Effect of Pd Location

CO2 Hydrogenation to Methanol on Pd-Cu Bimetallic Catalysts: H2/CO2 Ratio Dependence and Surface Species

The regulating effect of doping Cu on the catalytic performance of CO oxidative coupling to DMO on PdxCuy/GDY: A DFT study

Origin of Pd-Cu Bimetallic Effect for Synergetic Promotion of Methanol Formation from CO2 Hydrogenation

Optimal Icosahedral Copper-Based Bimetallic Clusters for the Selective Electrocatalytic CO2 Conversion to One Carbon Products

DFT Studies on Pt3M (M = Pt, Ni, Mo, Ru, Pd, Rh) Clusters for CO Oxidation

CO2 activation and dissociation on In2O3(110) supported PdnPt(4- n) (n = 0-4) catalysts: a density functional theory study

CO Oxidation Catalysed by Pd-based Bimetallic Nanoalloys

Tuning the intermediate reaction barriers by a CuPd catalyst to improve the selectivity of CO2 electroreduction to C2 products

Morphological and Compositional Design of Pd-Cu Bimetallic Nanocatalysts with Controllable Product Selectivity toward CO2 Electroreduction

Pd Atomic Layer Coating Enhances CO2 Hydrogenation to CH3OH Fuel on Cu@Pd(111) Core-Shell Structure Catalyst