High Pressure and Long-Term Gas Diffusion Coupled Damage of Composites Through a Multi-Physical Phase Field Framework

Pu-Song Ma,Lu-Wen Zhang

DOI: https://doi.org/10.1016/j.cma.2023.116006

2023-01-01

Abstract:In extreme service environments, composites are often exposed to high pressure and prolonged chemical penetration, leading to irreversible material damage and structural failure. To address this multi-field coupling problem that has long been a concern, we develop a theoretical framework for fully coupled stress distribution, gas diffusion, heat conduction, and damage evolution of composites to reproduce complex failure modes and disclose the damage mechanisms of composites in complicated environments. To verify the theoretical feasibility, the susceptibility of material fracture properties to hydrogen content is well revealed, and a typical problem, i.e., damage of multi-layered composite hydrogen storage vessels in distinct working stages, is investigated and discussed insightfully. We highlight that (i) the fracture phase field theory is rederived under the thermodynamic consistent framework; (ii) the proposed computational model can accurately capture the heat conduction response under the coupled effects of chemical diffusion and crack propagation; (iii) through a detailed analysis of the energy evolution, the model allows precise yield of the dominant mechanisms in the diverse damage stages of the materials. This study can reproduce the different damage patterns of composite structures under the action of multi-physical fields in extreme environments, thus providing a predictive computational approach to prevent disastrous failures.