Synthesis and properties of long chain polyesters from biobased 1,5-pentanediol and aliphatic α,ω-diacids with 10-16 carbon atoms

Lizhong Zhou,Linbo Wu,Pengkai Qin,Bo-Geng Li

DOI: https://doi.org/10.1016/j.polymdegradstab.2021.109546

IF: 5.204

2021-05-01

Polymer Degradation and Stability

Abstract:<p>Several aliphatic long chain polyesters with intrinsic viscosity of 0.80-1.47 dL/g were synthesized from biobased 1,5-pentanediol and long chain α,ω-diacids with 10-16 carbon atoms. Their chemical structure was characterized, and thermal, mechanical and gas barrier properties were assessed. These long chain polyesters have a melting temperature higher than poly(<em>ε</em>-caprolactone) and manifest polyethylene-like rapid crystallization, good thermal stability and ductile tensile behavior. Their melting temperature, crystallizablity, tensile modulus and oxygen and water vapor barrier performance all increase with increasing the chain length of diacid. In comparison with the widely used biodegradable poly(butylene adipate-co-terephthalate) copolyester, these potentially biodegradable polyesters show comparable tensile strength, ductility and oxygen barrier performance, but obviously superior crystallizability, tensile modulus and water vapor barrier performance.</p>

polymer science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to develop and evaluate a series of long - chain polyesters based on bio - based 1,5 - pentanediol (PeDO) and long - chain α,ω - dicarboxylic acids (containing 10 - 16 carbon atoms). Specifically, the research aims to:

1. **Synthesize new bio - based polyesters**: Synthesize a series of long - chain polyesters through melt polycondensation reaction. These polyesters have a relatively high intrinsic viscosity (0.80 - 1.47 dL/g) and are derived from renewable resources.

2. **Improve the thermal and mechanical properties of polyesters**: Improve the properties of polyesters such as melting point, crystallization ability and tensile modulus by extending the chain length of dicarboxylic acids, making them more suitable for practical applications.

3. **Improve gas barrier properties**: Study the performance of these polyesters in terms of water vapor and oxygen barrier to meet the requirements for their applications as packaging materials and mulch films.

4. **Compare with existing biodegradable polymers**: Compare these newly synthesized polyesters with widely used biodegradable copolyesters such as poly(butylene succinate - co - butylene terephthalate) (PBAT), and evaluate their advantages and disadvantages in terms of mechanical properties, gas barrier properties, etc.

### Main conclusions

Through the above research, the authors found that:
- These long - chain polyesters exhibit rapid crystallization and good tensile properties similar to polyethylene (PE).
- As the chain length of dicarboxylic acids increases, the melting point, crystallization ability, tensile modulus, and oxygen and water vapor barrier properties of polyesters all increase.
- Compared with PBAT, these potentially biodegradable polyesters are comparable in tensile strength, flexibility and oxygen barrier properties, but show obvious advantages in crystallization ability, tensile modulus (360 - 550 MPa vs. < 100 MPa) and water vapor barrier properties (2.4 - 5.9 times).

### Formula summary

- **Calculation formula for water vapor permeability (WVP)**:
\[
WVP=\frac{WVTR\cdot d}{P_0(RH_1 - RH_2)}
\]
where \(WVTR\) is the water vapor transmission rate, \(d\) is the film thickness, \(P_0\) is the saturated water vapor pressure (6630 Pa at 38 °C), and \(RH_1\) and \(RH_2\) are the relative humidities on both sides of the film respectively.

- **Calculation formula for oxygen transmission rate (OTR)**:
\[
OTR = \frac{P_{O2}\cdot\Delta P}{d}
\]
where \(P_{O2}\) is the oxygen permeability coefficient, \(\Delta P\) is the pressure difference on both sides of the film, and \(d\) is the film thickness.

Through these studies, the authors have shown that the overall properties of polyesters can be significantly improved by adjusting the chain length of dicarboxylic acids, providing new ideas for the development of high - performance bio - based polyesters.