Abstract:The control of the nanoscale composition and structure of alloy catalysts plays an important role in heterogeneous catalysis. This paper describes novel findings of an investigation for Pd-based nanoalloy catalysts (PdCo and PdCu) for ethanol oxidation reaction (EOR) in gas phase and alkaline electrolyte. Although the PdCo catalyst exhibits a mass activity similar to Pd, the PdCu catalyst is shown to display a much higher mass activity than Pd for the electrocatalytic EOR in alkaline electrolyte. This finding is consistent with the finding on the surface enrichment of Pd on the alloyed PdCu surface, in contrast to the surface enrichment of Co in the alloyed PdCo surface. The viability of C-C bond cleavage was also probed for the PdCu catalysts in both gas-phase and electrolyte-phase EOR. In the gas-phase reaction, although the catalytic conversion rate for CO2 product is higher over Pd than PdCu, the nanoalloy PdCu catalyst appears to suppress the formation of acetic acid, which is a significant portion of the product in the case of pure Pd catalyst. In the alkaline electrolyte, CO2 was detected from the gas phase above the electrolyte upon acid treatment following the electrolysis, along with traces of aldehyde and acetic acid. An analysis of the electrochemical properties indicates that the oxophilicity of the base metal alloyed with Pd, in addition to the surface enrichment of metals, may have played an important role in the observed difference of the catalytic and electrocatalytic activities. In comparison with Pd alloyed with Co, the results for Pd alloyed with Cu showed a more significant positive shift of the reduction potential of the oxygenated Pd species on the surface. These findings have important implications for further fine-tuning of the Pd nanoalloys in terms of base metal composition toward highly active and selective catalysts for EOR.

Insights into the Effect of Metal Ratio on Cooperative Redox Enhancement Effects over Au- and Pd-Mediated Alcohol Oxidation

Carbon-supported PdM (M = Au and Sn) Nanocatalysts for the Electrooxidation of Ethanol in High Ph Media

Au–Pd separation enhances bimetallic catalysis of alcohol oxidation

Theoretical Studies on the Synergetic Effects of Au–Pd Bimetallic Catalysts in the Selective Oxidation of Methanol

Optimising Surface D Charge of AuPd Nanoalloy Catalysts for Enhanced Catalytic Activity.

Synergy and Anti-Synergy between Palladium and Gold in Nanoparticles Dispersed on a Reducible Support

Modulating Electronic Structure of an Au‐Nanorod‐Core–PdPt‐Alloy‐Shell Catalyst for Efficient Alcohol Electro‐Oxidation

Preparation of Au@Pd Core–Shell Nanorods with fcc -2H- fcc Heterophase for Highly Efficient Electrocatalytic Alcohol Oxidation

Palladium (II)‐catalyzed homogeneous alcohol oxidations: Disclosing the crucial contribution of palladium nanoparticles in catalysis

Au–Pd Nanoparticles on Layered Double Hydroxide: Highly Active Catalyst for Aerobic Oxidation of Alcohols in Aqueous Phase

Maximizing the Synergistic Effect of PdAu Catalysts on TiO2(101) for Robust CO2 Reduction: A DFT Study

A Perspective on the Promoting Effect of Ir and Au on Pd Toward the Ethanol Oxidation Reaction in Alkaline Media

Steric Effects of Mesoporous Silica Supported Bimetallic Au-Pt Catalysts on the Selective Aerobic Oxidation of Aromatic Alcohols

Catalytic and electrocatalytic oxidation of ethanol over palladium-based nanoalloy catalysts

Revealing the Active Species for Aerobic Alcohol Oxidation by Using Uniform Supported Palladium Catalysts

Optimizing the Synergy Between Alloy and Alloy-Oxide Interface for CO Oxidation in Bimetallic Catalysts.

Origins for the Synergetic Effects of AuCu3 in Catalysis for Oxygen Reduction Reaction

Metal-Metal Oxide Catalytic Interface Formation and Structural Evolution: A Discovery of Strong Metal-Support Bonding, Ordered Intermetallics, and Single Atoms

Conjugated dual size effect of core-shell particles synergizes bimetallic catalysis

Manipulation of Neighboring Palladium and Mercury Atoms for Efficient *OH Transformation in Anodic Alcohol Oxidation and Cathodic Oxygen Reduction Reactions

Bimetallic Au-Pd NPs Embedded in MOF Ultrathin Nanosheets with Tuned Surface Electronic Properties for High-performance Benzyl Alcohol Oxidation