Control of Poly(glycerol sebacate) properties by varying levels of crosslinking using a fast microwave approach
Cc Lau,M Bayazit,J Knowles,J Tang
DOI: https://doi.org/10.3389/conf.FBIOE.2016.01.01811
IF: 5.7
2016-01-01
Frontiers in Bioengineering and Biotechnology
Abstract:Event Abstract Back to Event Control of Poly(glycerol sebacate) properties by varying levels of crosslinking using a fast microwave approach Chi Ching Lau1, Mustafa K Bayazit1, Jonathan Knowles2 and Junwang Tang1 1 University College London, Chemical Engineering, United Kingdom 2 UCL Eastman Dental Insitute, Biomaterials and Tissue Engineering, United Kingdom Introduction: Poly(glycerol sebacate) [PGS], a biopolymer, has shown some promising potentials as an implant in human body due to its predictable biodegradable properties[1],[2]. However, the preparation of PGS is very time-consuming and the reproducibility is always an issue[3]. Thus, alternative synthetic procedures are required to large scale controllable production of PGS. The main aim of this work is to reproducibly synthesise the PGS with controllable mechanical and thermal properties by varying levels of crosslinking using a scalable, economic and fast approach. Materials and Methods: Stoichiometric amounts of glycerol and sebacic acid were polymerized into prepolymers using microwave heating (MH) methods. For the cross-linking, the prepolymers were further cured in the vacuum oven at 120 ˚C for 24 to 48 hours. Results and Discussion: Consistent with previous studies, a viscous polymer is obtained upon ~74% polymerization, compared to a sticky elastomer for ~82% polymerization[3]. FTIR spectra of prepolymers with different degree of polymerisation prepared by MH show characteristic carbonyl stretching for PGS (νC=O) at 1740 cm-1, confirming polyesterification spectroscopically. By controlling the level of polymerization, PGS samples performed different mechanical properties which are crucial for biomedical applications. For example, prepared PGSMH (82%) showed lower Young’s modulus than PGSMH (74%), probably due to the level of cross-linking. Figure: (1) FTIR spectra of PGS samples (prepolymers), with ~74-82% of polymerization, prepared by microwave heating methods. (2) Young’s modulus of these prepolymer samples after a short curing period in vacuum oven at 120 ˚C. Conclusions: Therefore I have successfully prepared PGS with controllable cross-linking by MH method. Interestingly, this method was dramatically reduced the reaction time compared with the reported literature[1],[3], but it remained the same physical properties of the polymer. The tunable mechanical properties and cross-linking levels of PGS can be further applied in biomedical area, such as bone implants. References:[1] Y. Wang, G. Ameer, B. Sheppard, and R. Langer, “A tough biodegradable elastomer,” Nat. Biotechnol., vol. 20, no. June, 2002.[2] R. Rai, M. Tallawi, A. Grigore, and A. R. Boccaccini, “Synthesis, properties and biomedical applications of poly(glycerol sebacate) (PGS): A review,” Prog. Polym. Sci., vol. 37, no. 8, pp. 1051–1078, Aug. 2012.[3] X. Li, A. T.L. Hong, N. Naskar, and H.J. Chung, “Criteria for Quick and Consistent Synthesis of Poly(glycerol sebacate) for Tailored Mechanical Properties.,” Biomacromolecules, vol. 16, no. 5, pp. 1525–33, May 2015. Keywords: Biocompatibility, polymer, Biodegradable material, medical application Conference: 10th World Biomaterials Congress, Montréal, Canada, 17 May - 22 May, 2016. Presentation Type: New Frontier Oral Topic: Biodegradable polymers Citation: Lau C, Bayazit M, Knowles J and Tang J (2016). Control of Poly(glycerol sebacate) properties by varying levels of crosslinking using a fast microwave approach. Front. Bioeng. Biotechnol. Conference Abstract: 10th World Biomaterials Congress. doi: 10.3389/conf.FBIOE.2016.01.01811 Copyright: The abstracts in this collection have not been subject to any Frontiers peer review or checks, and are not endorsed by Frontiers. They are made available through the Frontiers publishing platform as a service to conference organizers and presenters. The copyright in the individual abstracts is owned by the author of each abstract or his/her employer unless otherwise stated. Each abstract, as well as the collection of abstracts, are published under a Creative Commons CC-BY 4.0 (attribution) licence (https://creativecommons.org/licenses/by/4.0/) and may thus be reproduced, translated, adapted and be the subject of derivative works provided the authors and Frontiers are attributed. For Frontiers’ terms and conditions please see https://www.frontiersin.org/legal/terms-and-conditions. Received: 27 Mar 2016; Published Online: 30 Mar 2016. Login Required This action requires you to be registered with Frontiers and logged in. To register or login click here. Abstract Info Abstract The Authors in Frontiers Chi Ching Lau Mustafa K Bayazit Jonathan Knowles Junwang Tang Google Chi Ching Lau Mustafa K Bayazit Jonathan Knowles Junwang Tang Google Scholar Chi Ching Lau Mustafa K Bayazit Jonathan Knowles Junwang Tang PubMed Chi Ching Lau Mustafa K Bayazit Jonathan Knowles Junwang Tang Related Article in Frontiers Google Scholar PubMed Abstract Close Back to top Javascript is disabled. Please enable Javascript in your browser settings in order to see all the content on this page.