Abstract:A novel trifluorovinyl-ether (-OCF=CF 2 , TFVE) functionalized diamine (DA-TFVE) with triarylmethane structure was successfully obtained from renewable vanillin through a Brönsted acidic ionic liquid catalyzed Friedel-Crafts reaction. Subsequently, traditional two-step condensations between DA-TFVE and dianhydride (6FDA and CBDA) were used to prepare two linear polyimides (PI-1 and PI-2, respectively) containing TFVE side groups. Both polyimides exhibited excellent film-forming ability and good solubility in common organic solvents. Upon heating, the linear polyimides could be transformed into cross-linked polyimides (cPI-1 and cPI-2) with perfluorocyclobutyl (PFCB) ether linkers through thermal [2π+2π] post-polymerization of TFVE groups. Surprisingly, both cPI-1 and cPI-2 exhibited high mechanical strength with a storage modulus of more than 2.0 GPa at room temperature, as well as outstanding thermal stability with a glass transition temperature of 402 °C and 374 °C, respectively. The polymer films before and after thermal crosslinking showed high transparency. In particular, a transmittance of 73% at 450 nm and 81% at 500 nm was observed for the colorless polyimide PI-2 with aliphatic segments. X-ray diffraction results of the obtained PIs showed that the average inter-chain distances (d-spacing) were 0.44 - 0.59 nm, indicating the hindered chain packing caused by PFCB linkers between the polymer chains. All these results suggested their potential application as candidate materials in high-performance packaging and flexible electronics.

Facile Synthesis of Soluble, Self-Crosslinkable and Crystalline Polyimides with Ultrahigh Thermal/chemical Resistance

Exceptionally thermostable and soluble aromatic polyimides with special characteristics: intrinsic ultralow dielectric constant, static random access memory behaviors, transparency and fluorescence

Synthesis and characterization of organo-soluble polyimides derived from a new spirobifluorene diamine

Synthesis of Highly Soluble and Transparent Polyimides

Solvent Resistant Self-Crosslinked Poly(ether Imide)

Novel Fluorinated Polyimides for Microelectronics Applications

Characterizations and Thermal Stability of Soluble Polyimide Derived from Novel Unsymmetrical Diamine Monomers

Synthesis and Properties of Novel Thermoplastic Polyimide

Synthesis and Characterization of Soluble Polyimides Based on a New Fluorinated Diamine: 4-Phenyl-2,6-bis[3-(4′-amino-2′-trifluoromethyl-phenoxy) Phenyl] Pyridine

Synthesis and Properties of Highly Organosoluble and Low Dielectric Constant Polyimides Containing Non-Polar Bulky Triphenyl Methane Moiety

Synthesis and characterization of fluorinated polyimides with high heat resistance and low dielectric constant

Synthesis and characterization of organosoluble polyfluorinated polyimides derived from 3,3′,5,5′-tetrafluoro-4,4′-diaminodiphenylmethane and various aromatic dianhydrides

Preparation and properties of melt-processable polyimides based on fluorinated aromatic diamines and aromatic dianhydrides

Facile Synthesis of A Symmetrical Diamine Containing Bis-Benzimidazole Ring and Its Thermally Stable Polyimides

Synthesis and Characterization of Novel Fluorinated Polyimides Derived from 4-Phenyl-2,6-bis[4-(4′-amino-2′-trifluoromethyl-phenoxy)phenyl]pyridine and Dianhydrides

Synthesis and characterization of novel polyimides derived from 2,6-bis[4-(3,4-dicarboxyphenoxy)benzoyl]pyridine dianhydride and aromatic diamines

Synthesis and characterization of novel fluorinated polyimides derived from 4,4′-[2,2,2-trifluoro-1-(3,5-ditrifluoromethylphenyl)ethylidene]diphthalic anhydride and aromatic diamines

Optically Transparent and Thermal‐Stable Polyimide Films Derived from a Semi‐Aliphatic Diamine: Synthesis and Properties

Soluble and Cross-Linkable Polyimides from a Vanillin-Derived Diamine: Preparation, Post-Polymerization and Properties

Colorless Semi-Alicyclic Copolyimides with High Thermal Stability and Solubility

Organo-Soluble Fluorinated Polyimides Derived from 4,4′-Bis (3-Amino-5-tri Uoromethylphenoxy)-3,3′,5,5′-tetramethyl Biphenyl (TFMDA) and Aromatic Dianhydrides