Abstract:A new aromatic, unsymmetrical ether diamine with a trifluoromethyl pendent group, 1,4-(2'-trifluoromethyl-4',4"-diaminodiphenoxy)benzene, was successfully synthesized in three steps with hydroquinone as a starting material and polymerized with various aromatic tetracarboxylic acid dianhydrides, including 4,4'-oxydiphthalic anhydride, 3,3,4,4'-benzophenone tetracarboxylic dianhydride, 2,2'-bis(3,4-dicarboxyphenyl)-hexafluoropropane dianhydride, and pyromellitic dianhydride, via a conventional two-step thermal or chemical imidization method to produce a series of fluorinated polyimides. The polyimides were characterized with solubility tests, viscosity measurements, IR, H-1 NMR, and C-13 NMR spectroscopy, X-ray diffraction studies, and thermogravimetric analysis. The polyimides had inherent viscosities of 0.56-0.77 dL/g and were easily dissolved in both polar, a protic solvents and common, low-boiling-point solvents. The resulting strong and flexible polyimide films exhibited excellent thermal stability, with decomposition temperatures (at 5% weight loss) above 522 degrees C and glass-transition temperatures in the range of 232-272 degrees C. Moreover, the polymer films showed outstanding mechanical properties, with tensile strengths of 74.5-121.7 MPa, elongations at break of 6-13%, and initial moduli of 1.46-1.95 GPa, and good dielectric properties, with low dielectric constants of 1.82-2.53 at 10 MHz. Wide-angle X-ray diffraction measurements revealed that these polyimides were predominantly amorphous. These outstanding combined features ensure that the polymers are desirable candidate materials for advanced microelectronic applications. (c) 2006 Wiley Periodicals, Inc.

Synthesis and characterization of organo-soluble polyimides derived from a new spirobifluorene diamine

Synthesis and characterization of organosoluble polyfluorinated polyimides derived from 3,3′,5,5′-tetrafluoro-4,4′-diaminodiphenylmethane and various aromatic dianhydrides

Synthesis and Properties of Novel Organosoluble Polyimides Derived from Bis[3-(4-amino-2-trifluoromethylphenoxy) Phenyl] Ether

Characterizations and Thermal Stability of Soluble Polyimide Derived from Novel Unsymmetrical Diamine Monomers

Synthesis and Characterization of Soluble Polyimides Derived from the Polycondensation of 2,6-Bis(4-amino-2-trifluoromethylphenoxy-4 '-Benzoyl)pyridine with Some Aromatic Dianhydrides

Organo-Soluble Fluorinated Polyimides Derived from 4,4′-Bis (3-Amino-5-tri Uoromethylphenoxy)-3,3′,5,5′-tetramethyl Biphenyl (TFMDA) and Aromatic Dianhydrides

Synthesis and Characterization of Novel Fluorinated Polyimides Derived from 4-Phenyl-2,6-bis[4-(4′-amino-2′-trifluoromethyl-phenoxy)phenyl]pyridine and Dianhydrides

Synthesis and Characterization of Soluble Polyimides Based on a New Fluorinated Diamine: 4-Phenyl-2,6-bis[3-(4′-amino-2′-trifluoromethyl-phenoxy) Phenyl] Pyridine

Organosolubility and Optical Transparency of Novel Polyimides Derived from 2′,7′-Bis(4-aminophenoxy)-spiro(fluorene-9,9′-xanthene)

Soluble Fluorinated Polyimides Derived from 1,4‐ (4′‐aminophenoxy)‐2‐(3′‐trifluoromethylphenyl)benzene and Aromatic Dianhydrides

Synthesis and Characterization of Soluble Polyimides Derived from a Novel Unsymmetrical Diamine Monomer: 1,4-(2′,4″-Diaminodiphenoxy)benzene

Synthesis and characterization of organosoluble ditrifluoromethylated aromatic polyimides

Synthesis and Properties of Fluorinated Polyimides from a New Unsymmetrical Diamine: 1,4‐(2′‐Trifluoromethyl‐4′,4′‐diaminodiphenoxy)benzene

Synthesis and Characterization of Novel Polyimides Derived from 1,1-Bis[4-(4′-aminophenoxy)phenyl]-1- [3″,5″-Bis(trifluoromethyl)phenyl]-2,2,2-trifluoroethane

Synthesis and Characterization of Highly Organosoluble Polyimides Based on a New Asymmetric Dianhydride

Synthesis and Properties of Novel Thermoplastic Polyimide

Preparation and Properties of Organo-Soluble Polyimides Based on 4,4 '-Diamino-3,3-dimethyldiphenylmethane and Conventional Dianhydrides

Synthesis And Characterization Of Porous Polyimide Films Containing Benzimidazole Moieties

Synthesis and Characterization of Biphenyl Polyimide Containing Alkyl Sulfide Structure

Synthesis and characterization of novel fluorinated polyimides derived from 4,4′-[2,2,2-trifluoro-1-(3,5-ditrifluoromethylphenyl)ethylidene]diphthalic anhydride and aromatic diamines

Studies on Organosoluble Polyimides Based on a Series of New Asymmetric and Symmetric Dianhydrides: Structure/solubility and Thermal Property Relationships