SOFC Cathode Material of La1.2Sr0.8CoO4± with a Fibrous Morphology: Preparation and Electrochemical Performance

Fushao Li,Yingxian Xu,Qingqing Wu,Deqiang Zhao,Mingsen Deng

DOI: https://doi.org/10.1016/j.ijhydene.2022.10.176

IF: 7.2

2023-01-01

International Journal of Hydrogen Energy

Abstract:Using soluble salts as metal-ion sources and polyacrylonitrile (PAN) as a polymer matrix, La1.2Sr0.8CoO4 +/- 6 cathode material with a fibrous morphology is prepared by electrostatic spinning, and microstructural characteristic of this material is investigated by field -emission scanning microscopy and X-ray diffraction. Electrochemical performance of the material in solid-oxide fuel cells is then tested. The results demonstrate that phase-pure La1.2Sr0.8CoO4 +/- 6 fibrils with tetragonal structure can be prepared from fresh silky pre-cursors using electrospinning after annealing at high temperature. Compared to the con-ventional cathode material that possesses a plain granular structure, La1.2Sr0.8CoO4 +/- 6 fibrilsUsing soluble salts as metal-ion sources and polyacrylonitrile (PAN) as a polymer matrix, La1.2Sr0.8CoO4 +/- 6 cathode material with a fibrous morphology is prepared by electrostatic spinning, and microstructural characteristic of this material is investigated by field -emission scanning microscopy and X-ray diffraction. Electrochemical performance of the material in solid-oxide fuel cells is then tested. The results demonstrate that phase-pure La1.2Sr0.8CoO4 +/- 6 fibrils with tetragonal structure can be prepared from fresh silky pre-cursors using electrospinning after annealing at high temperature. Compared to the con-ventional cathode material that possesses a plain granular structure, La1.2Sr0.8CoO4 +/- 6 fibrils exhibit superior electrochemical performance. At a temperature of 800 degrees C, the area specific resistance with this fibrous cathode is as low as 0.043 0 cm2, and maximum power density with the corresponding single-cell is 716 mW cm-2, demonstrating the fast electrode ki-netics in the O2 reduction reaction. Comparatively, the area specific resistance with the plain cathode is 0.062 0 cm2, and the maximum power density with the corresponding single-cell is only 642 mW cm-2. Under a constant voltage load of 0.6 V at a fixed tem-perature of 750 degrees C, the power output from a single-cell with the fiber-structured cathode maintains between 615 mW cm-2 and 585 mW cm-2 even after 15 h of running time, showing a slower fading rate and a more stable electrochemical performance than the plain cathode.(c) 2022 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.