Abstract:Ethanol oxidation reaction (EOR) is a common anode process for direct ethanol fuel cell (DEFC) and ethanol reforming electrolyzer. Au@Pt and AuPt alloy are widely used bimetallic catalysts, yet no comparative study has been reported of electrocatalysis of EOR on these two differently structured catalysts. The present work aims to synthesize and characterize carbon supported Au@Pt and AuPt with controlled composition and size, and compare their electrocatalytic activities and stabilities toward EOR in alkaline media. For the synthesis of Au@Pt/C, a 5-nm Au colloid was first obtained by adding excessive amount of sodium borohydride to a chloroauric acid precursor containing sodium citrate with a mixed ice-water bath. CO gas was bubbled into the Au colloidal solution at 60 degrees C under strong stirring to reduce a desired amount of potassium tetrachloroplatinate(II) to terminate Pt quasi-monolayer shell on Au nanoparticle core. A sonicated carbon black (Vulcan XC-72) aqueous slurry was then dropwise added to the above Au@Pt colloid, and the mixture was kept stifling for 48 h to ensure the exhaustive loading of Au@,Pt nanoparticles onto the carbon support. For the synthesis of AuPt/C with the same Au:Pt molar ratio and metal loading as that for Au@Pt/C, coreduction of the Au(III) and Pt(II) species was attained by using sodium borohydride as the reducing agent with the rest procedures being same as the above mentioned. X-ray diffractometry (XRD) revealed that the diffraction peaks for Au@Pt/C were virtually same as those for Au/C, consistent with a Pt quasi-monolayer, while the diffraction peaks for AuPt/C located in between those for Au/C and Pt/C. X-ray photoelectron spectroscopy (XPS) results were consitent with the different structures of the two catalysts, and the Pt core level shift suggested an upshift of Pt d-band center for both bimetallic catalysts. Cyclic voltammetry and chronoamperometry revealed markedly increased EOR current on Au@Pt/C and AuPt/C, as compared to that of Pt/C and Au/C. CO-stripping voltammetry on Au@Pt/C and AuPt/C indicated that surface reconstruction occurred by potential cycling, resulting in a decrease of ex- posed Pt sites but not the electrocatalytic activities. H-1 NMR analysis confirmed the C2 pathway is predominant. Nevertheless, Au@Pt/C outperformed AuPt/C and Pt/C with a lower onset oxidation potential and a higher peak current for EOR, as well as a slightly higher selectivity toward C1 pathway. Although the synergetic effect of Au-Pt bimetallic interface for EOR is not well understood, the enhanced adsorption of ethanol, OH, acetyl and CO on Pt sites may be accountable for the observed results.

Au Core@auptrh Alloy Shell Nanowires for Ethanol Oxidation

Highly Stable Pt–Au@Ru/C Catalyst Nanoparticles for Methanol Electro-oxidation

In situ assembly of ultrafine AuPd nanowires as efficient electrocatalysts for ethanol electroxidation

Platinum-Decorated Amorphous Sulfurized Palladium Nanowires for Effective Ethanol Oxidation Reaction

Trimetallic PdRhPt Porous Nanooctahedra As Highly Active and Cost‐Effective Electrocatalysts for Ethanol Electrooxidation

Pt-Sn alloy shells with tunable composition and structure on Au nanoparticles for boosting ethanol oxidation

Multimetallic AuPd@Pd@Pt Core-Interlayer-shell Icosahedral Electrocatalysts for Highly Efficient Oxygen Reduction Reaction

Modulating Electronic Structure of an Au‐Nanorod‐Core–PdPt‐Alloy‐Shell Catalyst for Efficient Alcohol Electro‐Oxidation

Ultrafine PdAgAu alloy nanowires for ethanol oxidation electrocatalysis

Trimetallic PtSnRh Wavy Nanowires As Efficient Nanoelectrocatalysts for Alcohol Electrooxidation.

Controlled Synthesis of Gold-Platinum Catalysts for Ethanol Electro-oxidation Reaction

Porous Pt Nanoframes Decorated with Bi(OH)3 As Highly Efficient and Stable Electrocatalyst for Ethanol Oxidation Reaction

Platinum-Cobalt Nanowires for Efficient Alcohol Oxidation Electrocatalysis

Sub-10 nm PdNi@PtNi Core–Shell Nanoalloys for Efficient Ethanol Electro-Oxidation

High-Yield Synthesis of Crystal-Phase-Heterostructured 4h/fcc Au@Pd Core-Shell Nanorods for Electrocatalytic Ethanol Oxidation

Core-shell Au@PtIr nanowires with dendritic alloy shells as efficient bifunctional catalysts toward methanol oxidation and hydrogen evolution reactions

OH Regulator of Amorphous CrOx on Defect‐Rich Ultrafine Pd Nanowires Boosts Electrocatalytic Ethanol Oxidation

Au/Pt Bimetallic Nanowires with Stepped Pt Sites for Enhanced C-C Cleavage in C2+ Alcohol Electro-oxidation Reactions

Electronic and Geometric Effects Endow PtRh Jagged Nanowires with Superior Ethanol Oxidation Catalysis

Engineering of Amorphous PtO x Interface on Pt/WO 3 Nanosheets for Ethanol Oxidation Electrocatalysis

Au@Ir core-shell nanowires towards oxygen reduction reaction