Abstract:The strength-ductility trade-off in steel, especially high-carbon steel, has been a long-standing and troubling issue; steel with increased mechanical properties has attracted much attention in recent years. In this study, an ultrafine-grained ultrastrong high-carbon steel with good ductility was produced by stabilizing retained austenite (RA) and accelerating carbide precipitation by warm rolling, quenching and tempering. The ultimate tensile strength reaches approximately 2550 MPa, with a total elongation of 5.1% after tempering at 220 ° C. The corresponding microstructure was composed of stable high-carbon RA and ultrafine-grained tempered martensite with carbide precipitates. The thermodynamic stability of RA was increased by carbon partitioning during quenching. The volume fraction was optimized to 6%. As the grain size of the primary austenite was refined to approximately 3 μm or smaller by warm rolling along the normal direction, the substructure of the high-carbon martensite was characterized as ultrafine twins and high-density dislocations. Carbide precipitations from the martensite matrix are accelerated at lower tempering temperatures. The main strengthening mechanism was still the strengthening of the solid solution and dislocations. Good tensile ductility was mainly derived from the effective weakening of the solid solution of martensite, whose carbon content decreased from 0.86 wt% to 0.61 wt%. Additionally, the greater ductility was attributed to the transformation-induced plasticity effect of larger amounts of high-carbon RA. These results may help in the design and production of ultrahigh strength and ductile high-carbon steel.

A Medium-C Martensite Steel with 2.6 GPa Tensile Strength and Large Ductility

A low-alloy high-carbon martensite steel with 2.6 GPa tensile strength and good ductility

Ultrahigh Ductility, High-Carbon Martensitic Steel

Strong and ductile medium-Mn steel achieved via controlled martensite tempering

A cryogenic ultra-strong and ductile steel induced by stable nanoscale dual-phase structure

Super-strong dislocation-structured high-carbon martensite steel

Light-weight Isometric-Phase Steels with Superior Strength-Hardness-ductility Combination

Enhanced mechanical properties of a high-carbon martensite steel processed by heavy warm rolling and tempering

An ultra-high-strength 12Mn maraging steel realized via nanoscale heterostructure engineering

Mechanical properties and deformation mechanisms of a novel austenite-martensite dual phase steel

Strengthening of Ultrafine Lamellar-Structured Martensite Steel Via Tempering-Induced Nanoprecipitation

Achieving ultrahigh strength by tuning the hierarchical structure of low-carbon martensitic steel

Super-High-Strength and Formable Medium Mn Steel Manufactured by Warm Rolling Process

Unusual step-like stress flow behavior and mechanisms of a 1.3 GPa grade medium-Mn steel with 51.2 % ductility

Mechanical Properties and Microstructures of A Novel Low Carbon High-Silicon Martensitic Steel

1.0 GPa Low Carbon Medium Mn Heavy Steel Plate with Excellent Ductility

Mechanical behavior and strengthening mechanism of a fine-grained medium carbon steel produced via cyclic oil quenching

High strength-toughness combination of a low-carbon medium-manganese steel plate with laminated microstructure and retained austenite

Strong Yet Ductile Medium Mn Steel Developed by Partial Austenitization

Ultrastrong Steel Strengthened by Multiple Shearable Nanostructures

Microstructure Evolution and Mechanical Properties of Medium Carbon Martensitic Steel during Warm Rolling and Annealing Process