Abstract:Producing biodegradable plastics from CO2 is a promising methodology for recycling industrial waste gas, and the conservation of environment and energy. Propylene oxide (PO) has been commonly used to copolymerize with CO2 to yield biodegradable poly(propylene carbonate) (PPC). PPC exhibits excellent transparency, low water and oxygen permeability as well as high flexibility. But low glass transition temperature (T-g) limited its practical applications. In recent years, the copolymerization of PO, CO2 with phthalic anhydride (PA) provides a robust and economical method to improve PPC's thermal and mechanical performance. In this study, to explore the relationship between the sequence structure and the properties of CO2/PO/PA terpolymer (PPC-P), PPC-P terpolymers with similar polyester (PE) content and molecular weight but different sequence structures (block, tapered and random) were synthesized through one-pot two-step method or one-pot one-step method using non-metallic catalytic system (TEB/PPNCI). The effects of polymerization temperature and reaction time on the composition and molecular weight of the PPC-P were systematically studied, and the PE content and molecular weight of all the terpolymers were controlled to be around 45% and 5.0x 10(4), respectively for comparison. The typical sequence structure characteristics of the terpolymers were proven by H-1-NMR. Differential scanning calorimetry (DSC), thermogravimetric analysis (TGA) and tensile test were used to characterize the thermal and mechanical properties of the PPC-P terpolymers. The block terpolymer shows two glass-transition temperature (T-g) (43 and 54 degrees C), while the tapered and random terpolymer has only one T-g (51, 50 degrees C). The T-d5 of the block terpolymer (263 degrees C) is lower than that of the tapered and random terpolymer (around 273 degrees C), indicating the poorer thermostability of block terpolymer. The three terpolymers with different sequence structures have similar tensile strength (around 35 MPa), all belonging to hard and brittle materials. [GRAPHICS] .

A new biodegradable CO2-based poly(ester-co-carbonate): Molecular chain building up with crosslinkable domain

Synthesis And Properties Of Long Chain Polyesters From Biobased 1,5-Pentanediol And Aliphatic Alpha,Omega-Diacids With 10-16 Carbon Atoms

Modification of Poly(ethylene 2,5-Furandicarboxylate) with Aliphatic Polycarbonate Diols: 1. Randomnized Copolymers with Significantly Improved Ductility and High CO2 Barrier Performance

Modification of Poly(ethylene furandicarboxylate) with Aliphatic Polycarbonate diols: 1. Randomnized Copolymers with Significantly Improved Ductility and High CO2 Barrier Performance

CO2 derived biodegradable polycarbonates: Synthesis, modification and applications

Biodegradable and Ultra-High Expansion Ratio PPC-P Foams Achieved by Microcellular Foaming Using CO2 as Blowing Agent

Architecting Branch Structure in Terpolymer of CO 2 , Propylene Oxide and Phthalic Anhydride: an Enhancement in Thermal and Mechanical Performances

Cross-Linked Networks in Poly(propylene Carbonate) by Incorporating (maleic Anhydride/cis-1,2,3,6-Tetrahydrophthalic Anhydride) Oligomer in CO2/Propylene Oxide Copolymerization: Improving and Tailoring Thermal, Mechanical, and Dimensional Properties

Design and syntheses of functional carbon dioxide-based polycarbonates via ternary copolymerization

Melt processable and biodegradable aliphatic polycarbonate derived from carbon dioxide and propylene oxide

Biodegradable PVC plasticizer derived from a new CO2-based Poly(carbonate-ester) macrodiol: Molecular design and plasticizing effect

Study of the Synthesis of CO<sub>2</sub>/Propylene Epoxide/Phthalic Anhydride Terpolymers with Different Sequence Structures and Their Properties

Enhanced Properties Of Biodegradable Poly(Propylene Carbonate)/Polyvinyl Formal Blends By Melting Compounding

Metal-Free Synthesis of Biodegradable CO2-Based Oligo(carbonate-ester) Diols As Building Blocks for Thermoplastic Polyurethanes

Synthesis And Properties Of Biodegradable Multiblock Poly(Ester-Carbonate) Comprising Of Poly(L-Lactic Acid) And Poly(Butylene Carbonate) With Hexamethylene Diisocyanate As Chain-Extender

A Green Method for Preparing Mechanically Robust Poly(propylene Carbonate) with Full Biodegradability Via Incorporating Hybrid Natural Filler

Synthesis of a Green Functional Carbon Dioxide‐based Polycarbonate Using Bio‐based Monomers

Cross-linkable and thermally stable aliphatic polycarbonates derived from CO 2 , propylene oxide and maleic anhydride

A novel biodegradable poly(propylene carbonate) with enhanced thermal and mechanical properties by incorporating tannic acid

Efficient and Scalable Synthesis of CO2‐Based Polycarbonate Diols With Difunctional Initiator and Proton Exchange Agent

Rheological, Thermal and Mechanical Properties of Biodegradable Poly(Propylene Carbonate)/Polylactide/Poly(1,2-Propylene Glycol Adipate) Blown Films