Abstract:Titania nanoparticles (NPs) find wide application in photocatalysis, photovoltaics, gas sensing, lithium batteries, etc. One of the most important synthetic challenges is maintaining control over the polymorph composition of the prepared nanomaterial. In the present work, TiO2 NPs corresponding to anatase, rutile, or an anatase/rutile/brookite mixture were obtained at 80 °C by an inverse microemulsion method in a ternary system of water/cetyltrimethylammonium bromide/1-hexanol in a weight ratio of 17:28:55. The only synthesis variables were the preparation of the aqueous component and the nature of the Ti precursor (Ti(IV) ethoxide, isopropoxide, butoxide, or chloride). The materials were characterized with X-ray diffraction, scanning/transmission electron microscopy, N2 adsorption-desorption isotherms, FTIR and Raman vibrational spectroscopies, and diffuse reflectance spectroscopy. The synthesis products differed significantly not only in phase composition, but also in crystallinity, textural properties, and adsorption properties towards water. All TiO2 NPs were active in the photocatalytic decomposition of rhodamine B, a model dye pollutant of wastewater streams. The mixed-phase anatase/rutile/brookite nanopowders obtained from alkoxy precursors showed the best photocatalytic performance, comparable to or better than the P25 reference. The exceptionally high photoactivity was attributed to the advantageous electronic effects known to accompany multiphase titania composition, namely high specific surface area and strong surface hydration. Among the single-phase materials, anatase samples showed better photoactivity than rutile ones, and this effect was associated, primarily, with the much higher specific surface area of anatase photocatalysts.

Simultaneous Tuning of Particle Size and Phase Composition of TiO2- Nanoparticles by a Simple Liquid Immiscibility Strategy

Preparation of TiO2 nanoparticles on the surface of SiO2 in binary liquids

Tuning Redistribution of CuO x Nanoparticles on TiO 2 Support

Tuning the Size of Photo-Deposited Metal Nanoparticles Via Manipulating Surface Defect Structures of TiO2 Nanocrystals.

Simultaneous regulation for phase transition of titanium dioxide and valence distribution of copper species on MnCuOx/TiSnOx

Modulating Surface Composition and Oxygen Reduction Reaction Activities of Pt–Ni Octahedral Nanoparticles by Microwave-Enhanced Surface Diffusion During Solvothermal Synthesis

Size- And Density-Controlled Synthesis Of Tio2 Nanodots On A Substrate By Phase-Separation-Induced Self-Assembly

Controllable Synthesis and Characterization of TiO_2/Pt Nanocomposite

Tuning and Understanding the Phase Interface of TiO2 Nanoparticles for More Efficient Lithium Ion Storage

Controllable Synthesis of Pt–Cu Nanocrystals and Their Tunable Catalytic Properties

Tuning of Catalytic CO Oxidation by Changing Composition of Rh-Pt Bimetallic Nanoparticles.

Precisely Controlled Heterogeneous Nucleation Sites for Tio2 Crystal Growth

Phase-Transition Engineering with Tuning of Defects in TiO 2 for Highly Efficient Electrochemical Nitrogen Reduction

Near Monodisperse TiO2 Nanoparticles and Nanorods.

Controllable One-Pot Synthesis and Enhanced Photocatalytic Activity of Mixed-Phase TiO2 Nanocrystals with Tunable Brookite/Rutile Ratios

Controllable One-Step Synthesis of Mixed-Phase TiO2 Nanocrystals with Equivalent Anatase/Rutile Ratio for Enhanced Photocatalytic Performance

TiO2 Nanoparticles with Adjustable Phase Composition Prepared by an Inverse Microemulsion Method: Physicochemical Characterization and Photocatalytic Properties

In Situ Tuning of Defects and Phase Transition in Titanium Dioxide by Lithiothermic Reduction

Novel TiO₂-Pt@SiO₂ nanocomposites with high photocatalytic activity

Synthesis of composition-tunable octahedral Pt–Cu alloy nanocrystals by controlling reduction kinetics of metal precursors

Achieving simultaneous Cu particles anchoring in meso-porous TiO2 nanofabrication for enhancing photo-catalytic CO2 reduction through rapid charge separation