Abstract:PtCu alloy nanocrystals, especially for the PtCu3 component, hold great potential as catalysts in methanol oxidation reaction (MOR) owing to their promising catalytic properties arising from the bifunctional mechanism associated with Pt and Cu sites. However, Pt and Cu salt precursors are difficult to be co-reduced in a synthesis due to the large difference in their redox potential, because of which Pt or Cu nanocrystals are initially generated and then evolve into a PtCu alloy with remarkable variation of the PtCu component by underpotential deposition (UPD) and galvanic replacement, respectively. Here we report a facile method for the shape-controlled synthesis of PtCu3 alloy nanocrystals by co-reduction of Pt and Cu salt precursors using oleylamine (OAm) and N,N-dimethylformamide (DMF) as co-reducing agents at different temperatures. PtCu3 alloy hexapods with preferential overgrowth along the <100> direction are obtained at 220 degrees C through co-reduction reaction accompanied by Cl- ion induced underpotential deposition (UPD). Meanwhile, galvanic replacement between PtCu3 alloy nanocrystals and the Pt precursor co-exists with overgrowth induced by co-reduction reaction at 190 degrees C, eventually resulting in PtCu3 hollow nanoframes. Both the PtCu3 alloy hexapods and hollow nanoframes exhibit remarkably enhanced catalytic properties in terms of activity and stability towards MOR relative to the commercial Pt/C. Specifically, the PtCu3 alloy hexapods and hollow nanoframes show the highest specific (2.96 mA cm(-2)) activity and mass activity (1.861 mA mu g(Pt)(-1)) for MOR, respectively, which are 13.5 and 24.2 times higher than those of the commercial Pt/C. This enhancement can be attributed to their unique structures and the possible bifunctional mechanism between Pt and Cu.

Synthesis of composition-tunable octahedral Pt–Cu alloy nanocrystals by controlling reduction kinetics of metal precursors

Composition-tunable synthesis of Pt–Cu octahedral alloy nanocrystals from PtCu to PtCu3 via underpotential-deposition-like process and their electro-catalytic properties

Controllable Synthesis of Pt–Cu Nanocrystals and Their Tunable Catalytic Properties

Underpotential Deposition-Induced Synthesis of Composition-Tunable Pt-Cu Nanocrystals and Their Catalytic Properties.

One-Pot Synthesis of Ternary Pt–Ni–Cu Nanocrystals with High Catalytic Performance

Kinetically Controlled Synthesis of Pt-Cu Alloy Concave Nanocubes with High-Index Facets for Methanol Electro-Oxidation

Facile Synthesis of Ptcu3 Alloy Hexapods and Hollow Nanoframes As Highly Active Electrocatalysts for Methanol Oxidation

Efficient Synthesis Of Bimetallic Pt3zn Alloy Nanocrystals With Different Shapes And Their Enhanced Electrocatalytic Activity

Tuning the Branches and Composition of PtCu Nanodendrites Through Underpotential Deposition of Cu Towards Advanced Electrocatalytic Activity

One-Step Synthesis of Hybrid Nanocrystals with Rational Tuning of the Morphology

Bimetallic Pd-Cu nanocrystals and their tunable catalytic properties.

Ratio-controlled Synthesis of CuNi Octahedra and Nanocubes with Enhanced Catalytic Activity.

Composition-tunable synthesis of Pt-Cu dendritic nanomaterials by ultrasound-assisted approach for highly efficient methanol oxidation

Mesoporous PtCu Alloy Nanoparticles with Tunable Compositions and Particles Sizes Using Diblock Copolymer Micelle Templates.

Composition-Tunable Ptcu Alloy Nanowires and Electrocatalytic Synergy for Methanol Oxidation Reaction

Synthesis of Pt–Ni Alloy Nanocrystals with High‐Index Facets and Enhanced Electrocatalytic Properties

Fine Tuning of the Structure of Pt-Cu Alloy Nanocrystals by Glycine-Mediated Sequential Reduction Kinetics

Bimetallic and Postsynthetically Alloyed PtCu Nanostructures with Tunable Reactivity for the Methanol Oxidation Reaction

Synthesis, shape control, and methanol electro-oxidation properties of Pt-Zn alloy and Pt3Zn intermetallic nanocrystals.

Synthesis and Characterization of Cu-Pt Bimetallic Nanoparticles

Synthesis and Characterization of Stable Cu-Pt Nanoparticles under Reductive and Oxidative Conditions