Remarkable Low-Temperature Hydrogen Cycling Kinetics of Mg Enabled by VH X Nanoparticles

Xuelian Zhang,Xin Zhang,Lingchao Zhang,Zhenguo Huang,Fang,Yaxiong Yang,Mingxia Gao,Hongge Pan,Yongfeng Liu
DOI: https://doi.org/10.1016/j.jmst.2022.10.029
2023-01-01
Abstract:Nanoscaled catalysts have attracted much more attention due to their more abundant active sites and better dispersion than their bulky counterparts. In this work, VHx nanoparticles smaller than 10 nm in average size are successfully synthesized by a simple solid-state ball milling coupled with THF washing process, which are proved to be highly effective in enhancing the hydrogen absorption/desorption kinetics of MgH2 at moderate temperatures. The nano-VHx-modified MgH2 releases hydrogen from 182 degrees C, which is 88 degrees C lower than additive-free MgH2. The release of hydrogen amounts to 6.3 wt% H within 10 min at 230 degrees C and 5.6 wt% H after 30 min at 215 degrees C with initial vacuum. More importantly, the dehydro-genated MgH2+ 10 wt.% nano-VHx rapidly absorbs 5.2 wt% H within 3 min at 50 degrees C under 50 bar H 2 . It even takes up 4.3 wt% H within 30 min at room temperature (25 degrees C) under 10 bar H 2 , exhibiting supe-rior hydrogenation kinetics to most of the previous reports. Mechanistic analyzes disclose the reversible transformation between V and V-H species during the hydrogen desorption-absorption process. The ho-mogeneously distributed V-based species is believed to act as hydrogen pump and nucleation sites for MgH2 and Mg, respectively, thus triggering fast hydrogenation/dehydrogenation kinetics.(c) 2022 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.
What problem does this paper attempt to address?