Abstract:A work-of-fracture method using three-point bend beam (3PBB) specimen, commonly employed to determine the fracture energy of concrete, is adapted to evaluate the mode-I cohesive fracture of fiber reinforced plastic (FRP) composite–concrete adhesively bonded interfaces. In this study, a bilinear damage cohesive zone model (CZM) is used to simulate cohesive fracture of FRP–concrete bonded interfaces. The interface cohesive process damage model is proposed to simulate the adhesive–concrete interface debonding; while a tensile plastic damage model is used to account for the cohesive cracking of concrete near the bond line. The influences of the important interface parameters, such as the interface cohesive strength, concrete tensile strength, critical interface energy, and concrete fracture energy, on the interface failure modes and load-carrying capacity are discussed in detail through a numerical finite element parametric study. The results of numerical simulations indicate that there is a transition of the failure modes controlling the interface fracture process. Three failure modes in the mode-I fracture of FRP–concrete interface bond are identified: (1) complete adhesive–concrete interface debonding (a weak bond), (2) complete concrete cohesive cracking near the bond line (a strong bond), and (3) a combined failure of interface debonding and concrete cohesive cracking. With the change of interface parameters, the transition of failure modes from interface debonding to concrete cohesive cracking is captured, and such a transition cannot be revealed by using a conventional fracture mechanics-based approach, in which only an energy criterion for fracture is employed. The proposed cohesive damage models for the interface and concrete combined with the numerical finite element simulation can be used to analyze the interface fracture process, predict the load-carrying capacity and ductility, and optimize the interface design, and they can further shed new light on the interface failure modes and transition mechanism which emulate the practical application.

Cohesive Zone Model Prediction of Debonding Failure in CFRP-to-steel Bonded Interface with a Ductile Adhesive

Finite Element Modeling of Debonding Failure in CFRP-strengthened Steel Beam Using a Ductile Adhesive

Cohesive Cracking Simulation of Concrete Using Effective Modulus

On adhesively bonded joints with a mixed failure mode-An experimental and numerical study

On Characterization of Cohesive Zone Model (CZM) Based Upon Digital Image Correlation (DIC) Method

A robust and efficient 3D mixed-mode cohesive interface model for predicting the debonding failure in FRP strengthened concrete structures

Cohesive Zone Model for Surface Cracks Using Finite Element Analysis

A cohesive zone model incorporating a Coulomb friction law for fiber-reinforced composites

Assessment of FRP-Concrete Interfacial Debonding with Coupled Mixed-Mode Cohesive Zone Model

A 2D Generic Multi-Surface Cohesive Zone Model for Simulating FRP-to-concrete Mixed-Mode Debonding Failure

Mixed-Mode Debonding Behavior Between CFRP Plates and Concrete under Fatigue Loading

An elastic-plastic cohesive zone model for metal-ceramic interfaces at finite deformations

Numerical Modelling of Bond Behaviour Between Steel and CFRP Laminates with a Ductile Adhesive

Estimation of fracture behavior of CFRP/CFRP adhesively bonded joints under mixed-mode conditions using a cohesive zone model

Nonlinear Semianalytical Prediction of Debonding at the FRP–Generic Material Interface with Mechanical End Anchorages

Discrete Cohesive Zone Model for Mixed-Mode Fracture Using Finite Element Analysis

A Combined Cohesive Elements—XFEM Approach for Analyzing Crack Propagation in Bonded Joints

Cohesive Fracture Simulation and Failure Modes of FRP–concrete Bonded Interfaces

Phase field-based cohesive zone approach to model delamination in fiber-reinforced polymer composites

A New Mechanism Based Cohesive Zone Model for Mode I Delamination Coupled with Fiber Bridging of Composite Laminates

A String-Based Cohesive Zone Model for Interlaminar Delamination