Abstract:AlCoCrFeNi 2.1 alloy, which belongs to the group of eutectic high-entropy alloys (EHEAs), possesses a combination of increased strength and ductility. It should retain these properties over a wide temperature range due to the high entropy effect of the system. At the same time, eutectic alloys are generally considered to have good castability, which increases the possibility of casting the alloy in larger volumes. One of the processes, that the alloy does not avoid when applied in industry, are the various joining techniques including electron beam welding. The weld area is often in a non-equilibrium state, which increases the risk of failure during operation. The paper therefore discusses the stability of the microstructure and mechanical properties of AlCoCrFeNi 2.1 alloy when exposed to short-term elevated temperatures. The material heated at 900 °C for 1 h in a vacuum furnace was observed using light and electron microscopy, analyzed for chemical and phase composition and finally subjected to HV0.1 hardness measurement and tensile strength test. The resulting condition was compared with the welded joint before exposure to elevated temperature. The microstructure of the weld was formed by a fine lamellar eutectic over the entire observed area. EBSD analysis confirmed the presence of a combination of FCC and BCC phases. The material hardness reached an average value of 370 HV0.1. Maximum tensile strength of the weld joint was measured at 944 MPa with the corresponding displacement of the crosshead 6.1 mm. The welded joint demonstrated sufficient stability and the ability to withstand short-term severe elevated temperature conditions.

Excellent corrosion resistance of electron beam welded joint and remelted layer of eutectic high-entropy alloy AlCoCrFeNi2.1

Microstructure and mechanical properties of electron beam welding of AlCoCrFeNi 2.1 eutectic high entropy alloy

A novel AlCo1.2Cr0.8FeNi2.1 eutectic high entropy alloy with excellent corrosion resistance

A Novel AlCo 1.2 Cr 0.8 FeNi 2.1 Eutectic High Entropy Alloy with Excellent Corrosion Resistance

Comparative Study of Mechanical and Corrosion Behaviors of Cost-Effective AlCrFeNi High Entropy Alloys

Corrosion behaviors and passive film properties of a newly developed cost-effective AlCrFeNi eutectic high entropy alloy in different corrosive solutions

Laser beam welding of AlCoCrFeNi2.1 eutectic high-entropy alloy

Corrosion resistant nanostructured eutectic high entropy alloy

Microstructure and mechanical properties of electron beam welded joints of GH3128 and CoCrFeNi high-entropy alloy

Microstructure and Corrosion Properties of Cr41CoFeNi Eutectic High-Entropy Alloy in Sulfuric Acid Solution

Thermal stability of electron beam welded AlCoCrFeNi 2.1 alloy

Study on the strengthening mechanism of AlCoCrFeNi2.1 eutectic high-entropy alloy

High-strength AlCoCrFeNi2.1 eutectic high entropy alloy with ultrafine lamella structure via additive manufacturing

Microstructural evolution, mechanical and corrosion behavior of an Al7.5Co20.5Fe24Ni24Cr24 high‐entropy alloy

Corrosion and passive behavior of Al0.8CrFeNi2.2 eutectic high entropy alloy in different media

Microstructural origins of high strength and high ductility in an AlCoCrFeNi2.1 eutectic high-entropy alloy

Simultaneously Enhanced Strength-Ductility of AlCoCrFeNi2.1 Eutectic High-Entropy Alloy Via Additive Manufacturing

A non-equiatomic FeNiCoCr high-entropy alloy with excellent anti-corrosion performance and strength-ductility synergy

Microstructure and mechanical properties of Co-free AlCrFeNiTi 0.2 eutectic high-entropy alloy

Microstructure and corrosion resistance of AlCrFeCuCo high entropy alloy

Preparation of Nano-bridged Honeycomb Microstructure Eutectic High-Entropy Alloy Coating with Excellent Corrosion Resistance by Laser Cladding