Abstract:The renewable nature, high carbon content, and unique hierarchical structure of wood-derived carbon make it an optimal self-supporting electrode for energy storage. However, the limitations in specific surface area and electrical conductivity defects pose challenges to achieving satisfactory charge storage in wood-derived carbon electrodes. Therefore, exploring diverse and effective surface strategies is crucial for enhancing the electrochemical energy storage performance. Herein, a decoration technique for enhancing aesthetic appeal involves applying a metal-organic framework (Ni/Co-MOF) containing nickel and cobalt onto the inner walls of wood tracheids. The sequential modification steps include carbonization, oxidation activation, and acid-etching. The Ni/NiO/CoO-CW-4 electrode, made by acid-etching carbonized wood (CW) doped with nickel, nickel oxide, and cobalt oxide for 4 h, has excellent surface area and pore size distribution, high graphitization degree, and exceptional conductivity. Furthermore, surface modification optimizes the surface chemistry and phase composition, resulting in a 0.8 mm thick Ni/NiO/CoO-CW-4 electrode with an exceptionally high areal capacitance of 16.76 F cm-2 at 5 mA cm-2. Meanwhile, the fabricated solid-state supercapacitor achieves an impressive energy density of 0.67 mWh cm-2 (8.38 mWh cm-3) at 2.5 mW cm-2 (31.25 mW cm-3), surpassing representative modified wood-based carbon electrodes by approximately 2-7 times. Additionally, the supercapacitor demonstrates exceptional stability, maintaining 96.21 % of capacitance even over 10,000 cycles. The parameters presented here demonstrate a significant improvement compared to those typically observed in most modified wood-derived carbon-based supercapacitors, effectively addressing common issues of low energy density and suboptimal cycling performance with wood carbon composites.

Wood-derived Scaffolds Decorating with Nickel Cobalt Phosphate Nanosheets and Carbon Nanotubes Used As Monolithic Electrodes for Assembling High-Performance Asymmetric Supercapacitor

A Metal-Organic Framework Derived Hierarchical Nickel-Cobalt Sulfide Nanosheet Array on Ni Foam with Enhanced Electrochemical Performance for Supercapacitors

A Zinc Cobalt Sulfide Nanosheet Array Derived from a 2D Bimetallic Metal-Organic Frameworks for High-Performance Supercapacitors

Mesoporous Ni2CoS4 Electrode Materials Derived from Coordination Polymer Bricks for High-Performance Supercapacitor

In Situsynthesis of Polyaniline/carbon Nanotube Composites in a Carbonized Wood Scaffold for High Performance Supercapacitors

Cobalt Hydroxide Nanosheets Grown on Carbon Nanotubes Anchored in Wood Carbon Scaffolding for High-Performance Hybrid Supercapacitors

Three-Dimensional Hierarchical Structure ZnO@C@NiO on Carbon Cloth for Asymmetric Supercapacitor with Enhanced Cycle Stability

Facile Electrodeposition of NiCo2O4 Nanosheets on Porous Carbonized Wood for Wood-Derived Asymmetric Supercapacitors

CNTs Support 2D NiMOF Nanosheets for Asymmetric Supercapacitors with High Energy Density

Facile synthesis of hierarchical porous manganese nickel cobalt sulfide nanotube arrays with enhanced electrochemical performance for ultrahigh energy density fiber-shaped asymmetric supercapacitors

In situ growth of N/O-codoped carbon nanotubes in wood-derived thick carbon scaffold to boost the capacitive performance

Surface-modified composites of metal-organic framework and wood-derived carbon for high-performance supercapacitors

Three-dimensional hierarchical NiCo2O4 nanowire@Ni3S2 nanosheet core/shell arrays for flexible asymmetric supercapacitors

Three-Dimensional Nico2o4@Mnmoo4 Core-Shell Nanoarrays for High-Performance Asymmetric Supercapacitors

Free-standing electrodes via coupling nanostructured Ni–NiO with hierarchical wood carbon for high-performance supercapacitors and Ni–Zn batteries

Multilayer Core-Sheath Wires with Cus Nanosheet Arrays and Pedot Sheaths for High-Performance Fiber-Shaped Asymmetric Supercapacitors

NiCo2O4 nanosheet stereostructure with N-doped carbon/Co array supports derived from Co-MOF for asymmetric supercapacitor

Mushroom-like Cobalt Nickle Metaphosphate@nickel Diselenide Core–shell Nanorods for Asymmetric Supercapacitors

Three-dimensional NiCo2O4 nanosheets arrays on carbon nanofibers for high-performance asymmetric solid-state supercapacitor

MOF-derived NiZnCo-P nano-array for asymmetric supercapacitor

One-step electrodeposited cracked-bark-shaped NiCoMoS on carbon cloth for high-performing aqueous asymmetric supercapacitors