Abstract:TiO2-ZrO2 (Ti-Zr) carrier was prepared by a co-precipitation method and 1 wt. % V2O5 and 0.2 CeO2 (the Mole ratio of Ce to Ti-Zr) was impregnated to obtain the V2O5-CeO2/TiO2-ZrO2 catalyst for the selective catalytic reduction of NOx by NH3. The transient activity tests and the in situ DRIFTS (diffuse reflectance infrared Fourier transform spectroscopy) analyses were employed to explore the NH3-SCR (selective catalytic reduction) mechanism systematically, and by designing various conditions of single or mixing feeding gas and pre-treatment ways, a possible pathway of NOx reduction was proposed. It was found that NH3 exhibited a competitive advantage over NO in its adsorption on the catalyst surface, and could form an active intermediate substance of -NH2. More acid sites and intermediate reaction species (-NH2), at lower temperatures, significantly promoted the SCR activity of the V2O5-0.2CeO2/TiO2-ZrO2 catalyst. The presence of O2 could promote the conversion of NO to NO2, while NO2 was easier to reduce. The co-existence of NH3 and O2 resulted in the NH3 adsorption strength being lower, as compared to tests without O2, since O2 could occupy a part of the active site. Due to CeO2’s excellent oxygen storage-release capacity, NH3 adsorption was weakened, in comparison to the 1 wt. % V2O5-0.2CeO2/TiO2-ZrO2 catalyst. If NOx were to be pre-adsorbed in the catalyst, the formation of nitrate and nitro species would be difficult to desorb, which would greatly hinder the SCR reaction. All the findings concluded that NH3-SCR worked mainly through the Eley-Rideal (E-R) mechanism.

Boosting the Catalytic Performance of Fe/Zr Catalyst by Tungsten Addition for Selective Catalytic Reduction of NOx with Ammonia

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

New insight on optimization of acid promoter over Fe/Zr catalyst for selective catalytic reduction of NOx with NH3

Selective Catalytic Reduction of NOx with NH3 over Short-Range Ordered W-O-Fe Structures with High Thermal Stability

New insight on optimization of acid promoter over Fe/Zr catalyst for selective catalytic reduction of NO with NH3

Activity Enhancement of Wo3 Modified Fe2o3 Catalyst for the Selective Catalytic Reduction of Nox by Nh3

Effect of Fe2O3 on ZrTiO4 Support for NH3-SCR Catalytic Performance

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

Superior Performance of Fe1-xWxOδ for the Selective Catalytic Reduction of NOx with NH3: Interaction Between Fe and W.

Influence of WO3 Doping on Properties of V2O5/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx by NH3

Optimizing Selective Catalytic Reduction of NO with NH3 on Fe2O3/WO3 Via Redox‐Acid Synergy

The promoting mechanism of in situ Zr doping on the hydrothermal stability of Fe-SSZ-13 catalyst for NH3-SCR reaction

MnOx-Decorated Fe–Zr-Based Nano-Catalysts for Low-Temperature NH3-SCR: Improvement of Catalytic Activity

Experimental and Density Functional Theory Studies on the Zeolite-Based Fe–Ni–W Trimetallic Catalyst for High-Temperature NOx Selective Catalytic Reduction: Identification of Active Sites Suppressing Ammonia Over-oxidation

Effect of iron loading on the performance and structure of Fe/ZSM-5 catalyst for the selective catalytic reduction of NO with NH3

Promotional Effects of Titanium Additive on the Surface Properties, Active Sites and Catalytic Activity of W/CeZrOx Monolithic Catalyst for the Selective Catalytic Reduction of NOx with NH3

Tungsten Modified MnOx–CeO2/ZrO2 Monolith Catalysts for Selective Catalytic Reduction of NOx with Ammonia

Promoting effect of Cu and Mn doping on the Fe/ZSM-5 catalyst for selective catalytic reduction of NO with NH 3

Promotional Roles of ZrO2 and WO3 in V2O5-WO3/TiO2-ZrO2 Catalysts for NOx Reduction by NH3:Catalytic Performance, Morphology, and Reaction Mechanism

Activity enhancement of WO3 modified FeTiO catalysts for the selective catalytic reduction of NO by NH3

Activity enhancement of WO<sub>3</sub> modified FeTiO<sub>x</sub> catalysts for the selective catalytic reduction of NO<sub>x</sub> by NH<sub>3</sub>