Enhanced low-temperature performance of Al-rich Cu-SSZ-13 by Ce modification upon hydrothermal aging for NH 3 -SCR
Yali Shen,Tiantian Li,Jing Yang,Aiyong Wang,Li Wang,Wangcheng Zhan,Yanglong Guo,Yun Guo
DOI: https://doi.org/10.1016/j.cej.2023.145275
IF: 15.1
2023-08-16
Chemical Engineering Journal
Abstract:3wt.% Cu/SSZ-13 (Cu 3 /Z) and Ce modified 3wt.% Cu/SSZ-13 (Ce-Cu 3 /Z) catalysts were prepared and then hydrothermally aged. The Ce-modified Ce-Cu 3 /Z catalyst revealed excellent NH 3 -SCR activity and hydrothermal stability. Combined with a series of characterizations, it was proved that the introduction of Ce could inhibit the dealumination, and prevent the aggregation of Cu ions to form CuO x and CuAl 2 O 4 species upon hydrothermal aging, thus improving the hydrothermal stability of Ce-Cu 3 /Z. In addition, Ce could interact with Cu species to enhance the reducibility of catalyst, and the interaction between Ce and Cu species was strengthened after hydrothermal aging. Also, the presence of Ce species could enhance the NH 3 and NO x adsorption capacity of the catalyst, resulting in higher NH 3 -SCR activity of Ce-Cu 3 /Z after hydrothermaly aged at 700 °C. In situ DRIFTS results showed that the NH 3 -SCR reaction followed both E-R and L-H mechanisms on the Cu 3 /Z-700 and Ce-Cu 3 /Z-700 catalysts at 150 °C. Ce doping could promote the formation of L-NH 3 (NH 3 species coordinated to Lewis acid sites) and nitrate species on the Ce-Cu 3 /Z-700 catalyst, as well as the involvement of L-NH 3 in the reaction, which play a crucial role as the main active intermediates at low temperature.
engineering, chemical, environmental