Abstract:Giant dielectric (GD) oxides exhibiting extremely large dielectric permittivities (ε' > 104) have been extensively studied because of their potential for use in passive electronic devices. However, the unacceptable loss tangents (tanδ) and temperature instability with respect to ε' continue to be a significant hindrance to their development. In this study, a novel GD oxide, exhibiting an extremely large ε' value of approximately 7.55 × 104 and an extremely low tanδ value of approximately 0.007 at 103 Hz, has been reported. These remarkable properties were attributed to the synthesis of a Lu3+/Nb5+ co-doped TiO2 (LuNTO) ceramic containing an appropriate co-dopant concentration. Furthermore, the variation in the ε' values between the temperatures of -60 °C and 210 °C did not exceed ±15% of the reference value obtained at 25 °C. The effects of the grains, grain boundaries, and second phase particles on the dielectric properties were evaluated to determine the dielectric properties exhibited by LuNTO ceramics. A highly dense microstructure was obtained in the as-sintered ceramics. The existence of a LuNbTiO6 microwave-dielectric phase was confirmed when the co-dopant concentration was increased to 1%, thereby affecting the dielectric behavior of the LuNTO ceramics. The excellent dielectric properties exhibited by the LuNTO ceramics were attributed to their inhomogeneous microstructure. The microstructure was composed of semiconducting grains, consisting of Ti3+ ions formed by Nb5+ dopant ions, alongside ultra-high-resistance grain boundaries. The effects of the semiconducting grains, insulating grain boundaries (GBs), and secondary microwave phase particles on the dielectric relaxations are explained based on their interfacial polarizations. The results suggest that a significant enhancement of the GB properties is the key toward improvement of the GD properties, while the presence of second phase particles may not always be effective.

Enhanced Dielectric Performance of Niobium and Thulium Modified Rutile TiO2 Ceramics by Defect Regulation

Enhanced dielectric performance of Niobium and Thulium modified rutile TiO 2 ceramics by defect regulation

Colossal Permittivity and Ultralow Dielectric Loss in Nb-doped SrTiO 3 Ceramics

Colossal Permittivity and Low Dielectric Loss in Niobium and Europium Co-Doped TiO2 Ceramics by Adding B2O3

Colossal Dielectric Permittivity in (al+nb) Co-Doped Ba0.4Sr0.6TiO3 Ceramics

Columbite-rich Multiphase TiO2 Nanoceramic with Superior Mechanical and Dielectric Properties

High Dielectric Permittivity and Ultralow Dielectric Loss in Nb-doped SrTiO3 Ceramics

High dielectric permittivity and ultralow dielectric loss in Nb-doped SrTiO 3 ceramics

Enhanced dielectric properties and improved thermal stability in TiO 2 -based ceramics by Cu and Nb co-doping

Defect engineering in rare‐earth‐doped BaTiO 3 ceramics: Route to high‐temperature stability of colossal permittivity

Microstructural Evolution and High-Performance Giant Dielectric Properties of Lu3+/Nb5+ Co-Doped TiO2 Ceramics

Colossal permittivity and ultralow dielectric loss in SrTi1-Nb O3 ceramics sintered at different atmospheres via defect chemistry improvement

Defect chemistry and optimized dielectric properties of Ni1-8O ceramics via doping donor ions

Origin of Colossal Dielectric Permittivity of Rutile Ti0.9In0.05Nb0.05O2: Single Crystal and Polycrystalline

Bismuth Oxide Modified Europium and Niobium Co-Doped Titanium Dioxide Ceramics: Colossal Permittivity and Low Dielectric Loss Design

Colossal Dielectric Performance of Pure Barium Titanate Ceramics Consolidated by Spark Plasma Sintering

Frequency and Temperature Independent (nb0.5ga0.5)x(ti0.9zr0. 1)1-Xo2 Ceramics with Giant Dielectric Permittivity and Low Loss

Thermal stable and ultralow dielectric loss in (Gd0.5Ta0.5) Ti1-O2 giant permittivity ceramics by defect engineering

High Insulation Resistivity and Ultralow Dielectric Loss in La-Doped SrTiO3 Colossal Permittivity Ceramics through Defect Chemistry Optimization

Novel SrTiO 3 -based ceramics with colossal permittivity, low dielectric loss, and high insulation resistivity via defect engineering

The Dielectric Properties for (nb,in,b) Co-Doped Rutile TiO2 Ceramics