Improvement of Breakdown Performance of Long-chain Branched Polypropylene for Film Capacitors Based on Crystallization Control

Zhaoliang Xing,Shaowei Guo,Mengdie Zhang,Meng Xiao,Boxue Du,Chong Zhang,Huize Cui,Xiying Dai,Fei Li

DOI: https://doi.org/10.1109/ceidp55452.2022.9985351

2022-01-01

Abstract:The breakdown strength of polypropylene (PP) films for metallized film capacitors will reduce when subjected to high temperature in practical applications, which is likely to cause equipment failures. This paper proposed a method to improve the breakdown strength of films by introducing long-chain branches to regulate the molecular structure and adding different contents of the NA-21 nucleating agent to control crystallization. The results show that long-chain branches can hinder the movement of molecular chains and improve thermal stability. Furthermore, the addition of the NA-21 nucleating agent promotes the crystallization of long-chain branched polypropylene (LCBPP) and affects its crystalline morphology. The carrier transport process is limited in the modified material with nucleating agents added, and the conductivity loss of the film is reduced. At $125 ^{\circ}\text{C}$, compared with PP, the breakdown strength of the modified film with 0.05 wt% NA-21 content increased by 108.6 kV/mm. This method has potential in the application of film capacitors.