Synergistic Effect of O2 and H2S on the Corrosion Behavior of N80 Steel in a Simulated High-Pressure Flue Gas Injection System
Kexi Liao,Feilong Zhou,Xiaoqin Song,Yanran Wang,Shuai Zhao,Jianjun Liang,Long Chen,Guoxi He
DOI: https://doi.org/10.1007/s11665-019-04512-2
IF: 2.3
2020-01-01
Journal of Materials Engineering and Performance
Abstract:The aim of this work was to understand the synergistic effect of O<sub>2</sub> and H<sub>2</sub>S on the corrosion behavior of N80 steel in a simulated high-pressure flue gas injection system. Weight loss measurements show that the presence of O<sub>2</sub> and an increase in temperature significantly accelerated the general corrosion rate of the N80 steel. We calculated a gray relational grade between different impact factors and the general corrosion rate from the results of an orthogonal experimental corrosion rate. The grade ranking of impact factors was: O<sub>2</sub> concentration (0.817) > temperature (0.706) > total pressure (0.689) > H<sub>2</sub>S concentration (0.665) > CO<sub>2</sub> concentration (0.517). Surface characterization of corrosion scales was done using scanning electron microscopy, energy-dispersive spectroscopy, x-ray powder diffraction, and 3D optical microscope analysis. The results show that in the O<sub>2</sub>-H<sub>2</sub>S-CO<sub>2</sub>-H<sub>2</sub>O coexistence system the products were composed mainly of FeCO<sub>3</sub>, FeS, Fe<sub>2</sub>O<sub>3</sub>, Fe<sub>3</sub>O<sub>4</sub>, and elemental sulfur. The results of the corrosion rate test and the characterization show that the presence of O<sub>2</sub> greatly accelerated the corrosion process and changed the corrosion mechanism. Elemental sulfur, which was generated by the reaction between the H<sub>2</sub>S and the O<sub>2</sub>, participated in the corrosion process of the N80 steel. It could be considered that the synergistic effect of O<sub>2</sub> and H<sub>2</sub>S accelerated the corrosion of the N80 steel. In addition, the porous structures of the corrosion scales and the severe local pits show that the high content of O<sub>2</sub> inhibited the formation of FeCO<sub>3</sub> and aggravated the corrosion of N80 steel.
materials science, multidisciplinary