Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

Effect of Pseudomonas Sp. on Simulated Tidal Corrosion of X80 Pipeline Steel.

Marine tidal corrosion of X80 pipeline steel under federative action of Pseudomonas sp. and Desulfovibrio desulfuricans

Differential Stimulation of Somatostatin but Not Neuropeptide Y Gene Expression by Quinolinic Acid in Cultured Cortical Neurons

Effects of Pseudomonas aeruginosa on EH40 steel corrosion in the simulated tidal zone

Low?efficiency of cathodic protection in marine tidal corrosion of X80 steel in the presence of Pseudomonas sp

Corrosion inhibition of deposit-covered X80 pipeline steel in seawater containing Pseudomonas stutzeri.

Accelerated tidal corrosion of X80 pipeline steel by Desulfovibrio desulfuricans

Microbial corrosion behavior of pipeline steels in simulation environment of natural gas transportation pipeline

Influence of anion and sulfate-reducing bacteria on the stress corrosion behavior and mechanism of X70 steel in a marine mud environment

A study on the microbial biocorrosion behavior of API 5 L X65 carbon steel exposed to seawater

Methanogenic Archaea and Sulfate Reducing Bacteria Induce Severe Corrosion of Steel Pipelines after Hydrostatic Testing

Effect of nutrient concentration on corrosion mechanism of X80 pipeline steel caused by sulfate-reducing bacteria

Stress corrosion behavior of X80 pipeline steel in natural seawater with different dissolved oxygen

Corrosion of Pseudomonas aeruginosa toward a Cu–Zn–Ni alloy inhibited by the simulative tidal region

Determinants of health-promoting lifestyles in older persons.

Accelerated biocorrosion of stainless steel in marine water via extracellular electron transfer encoding gene phzH of Pseudomonas aeruginosa

Microbiologically influenced corrosion of steel in coastal surface seawater contaminated by crude oil

Insight into sulfate-reducing bacteria corrosion behavior of X80 pipeline steel welded joint in a soil solution

Effect of Ochrobactrum sp. on the Corrosion Behavior of 10MnNiCrCu Steel in Simulated Marine Environment

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

Corrosion Behavior of X80 Steel in a Simulated Soil Solution Under Square-Wave Current Interference