The Collaborative Effect of Carbon-Borides and the Redistribution of Ni, Cr and Mo on the Corrosion and Wear Resistance of Nicrmo Coatings by Laser Cladding
Xiaofeng Zhao,Hongzhi Cui,Di Jiang,Xiaojie Song,Hao Chen,Guoliang Ma,Zeliang Yin,Yuming Zhu,Hushan Niu,Baocheng Li,Jun Cui
DOI: https://doi.org/10.2139/ssrn.4160332
2022-01-01
Abstract:In this study, NiCrMo coatings with different contents of B and C have been prepared by laser cladding. Based on passive elements Ni, Cr and Mo, on the one hand, the matrix of coatings could be formed, on the other hand, hierarchical carbides, borides and even carbon-borides could be obtained. The object here was to improve both wear resistance and corrosion resistance. Thus, the phases, microstructure, microhardness, fracture features, and wear and corrosion resistance were thoroughly analyzed. The results showed that the phases transformed from single FCC to FCC + carbon-borides after adding B 4 C, and eutectic structure composed of alternating FCC and carbo-borides appears in interdendritic regions. With the increasing of B 4 C content, due to the gradual increase of carbon-borides, grain refinement and eutectic structure in interdendritic regions, the microhardness of coatings increased significantly, which further enhanced their wear resistance, and the fracture mode changed from ductile fracture to brittle fracture. It is noteworthy that, the formation of moderate amount of carbides, borides and carbon-borides which derived from B 4 C, also improved the corrosion resistance, instead of cause deterioration, which attributed to the coherent relationship of carbon-borides and the matrix, and together with the redistribution of Ni, Cr and Mo, as well as the combined action of multiple reinforcing mechanisms.