Abstract:CeO2 nanoparticles are loaded onto atomically dispersed Fe‐NC materials (CeO2@Fe‐NC). The CeO2 is found to facilitate the formation of intermediates during the oxygen reduction reaction, accelerate the reaction kinetics and effectively eliminate H2O2. Consequently, the CeO2@Fe‐NC catalyst exhibits satisfactory activity (half‐wave potential of 0.89 V and limiting current density of 6.2 mA cm–2) and significantly improved stability (only 1% decline after 10 000 cycles). The Fenton reaction, induced by the H2O2 formed during the oxygen reduction reaction (ORR) process leads to significant dissolution of Fe, resulting in unsatisfactory stability of the iron–nitrogen‐doped carbon catalysts (Fe‐NC). In this study, a strategy is proposed to improve the ORR catalytic activity while eliminating the effect of H2O2 by introducing CeO2 nanoparticles. Transmission electron microscopy and subsequent characterizations reveal that CeO2 nanoparticles are uniformly distributed on the carbon substrate, with atomically dispersed Fe single‐atom catalysts (SACs) adjacent to them. CeO2@Fe‐NC achieves a half‐wave potential of 0.89 V and a limiting current density of 6.2 mA cm−2, which significantly outperforms Fe‐NC and commercial Pt/C. CeO2@Fe‐NC also shows a half‐wave potential loss of only 1% after 10 000 CV cycles, which is better than that of Fe‐NC (7%). Further, H2O2 elimination experiments show that the introduction of CeO2 significantly accelerate the decomposition of H2O2. In situ Raman spectroscopy results suggest that CeO2@Fe‐NC significantly facilitates the formation of ORR intermediates compared with Fe‐NC. The Zn–air batteries utilizing CeO2@Fe‐NC cathodes exhibit satisfactory peak power density and open‐circuit voltage. Furthermore, theoretical calculations show that the introduction of CeO2 enhances the ORR activity of Fe‐NC SAC. This study provides insights for optimizing SAC‐based electrocatalysts with high activity and stability.

Stabilization of oxidation state in ZnO decorated-CeO2 for enhanced formation of CO in CO2 electroreduction

Rational Design and Synergistic Effect of Ultrafine Ag Nanodots Decorated Fish-Scale-like Zn Nanoleaves for Highly Selective Electrochemical CO2 Reduction

A Universal Method to Engineer Metal Oxide-Metal-Carbon Interface for Highly Efficient Oxygen Reduction.

Oxygen vacancy enhancing CO2 electrochemical reduction to CO on Ce-doped ZnO catalysts

CeO2-modified Cu electrode for efficient CO2 electroreduction to multi-carbon products

In Situ Symbiosis of Cerium Oxide Nanophase for Enhancing the Oxygen Electrocatalysis Performance of Single‐Atom Fe─N─C Catalyst with Prolonged Stability for Zinc–Air Batteries

Ag/ZnO composite structure modulated by hybrid engineering for efficient electroreduction of CO2 to CO

Fabrication of ZnO nanosheets self-assembled by nanoparticles for accelerated electrocatalytic reduction of CO2 to CO

Stabilizing the oxidation state of catalysts for effective electrochemical carbon dioxide conversion

Enhanced High-Temperature CO2 Electrolysis on CeO2 by Inducing Under-Coordinated Dual-Atom Active Sites

CeOx Promoted Electrocatalytic CO2 Reduction to Formate by Assisting in the Critical Hydrogenation Step

Enhancing CO2 Electroreduction with the Metal-Oxide Interface

CO2-Induced Fibrous Zn Catalyst Promotes Electrochemical Reduction of CO2 to CO

Modulating Surface Zinc Species Via Facet Engineering for Efficient Electroreduction of CO2 to CO

Modifying Redox Properties and Local Bonding of Co3O4 by CeO2 Enhances Oxygen Evolution Catalysis in Acid

Boosting CO 2 Electroreduction via Construction of a Stable ZnS/ZnO Interface

Nanostructuring Matters: Stabilization of Electrocatalytic Oxygen Evolution Reaction Activity of ZnCo2O4 by Zinc Leaching

Interface interaction of Ag-CeO2-Co3O4 facilitate ORR/OER activity for Zn-air battery

Enhanced electroreduction of CO2 to C2+ products on heterostructured Cu/oxide electrodes

Ce3+/Ce4+ Ion Redox Shuttle Stabilized Cuδ+ for Efficient CO2 Electroreduction to C2H4

Enhanced high-temperature CO 2 electrolysis on CeO 2 by inducing under-coordinated dual-atom active sites