Preparation and Up-Conversion Luminescence of Three-Dimensional Er3+/Yb3+ Co-Doped AlN Nanowire Networks

Jiaqi Wang,Hongwei Zou,Dongfang Zhao,Yiyi Zhang,Mei Chen,Huiling Zheng,Xuejiao Wang,Chuang Wang,Qiushi Wang,Ge Zhu
DOI: https://doi.org/10.1016/j.mssp.2022.107186
IF: 4.1
2023-01-01
Materials Science in Semiconductor Processing
Abstract:Up-conversion (UC) nanomaterials have attracted extensive attention due to their unique optical properties and potential in many different applications. Here, novel three-dimensional Er3+/Yb3+ co-doped AlN (AlN:Yb3+, Er3+) nanowire networks were synthesized for the first time using the arc-discharge process. The branched nanowires in networks show a very regular directional relationship: the included angles of the branches are 60 or 120 degrees. A growth mechanism of nanowire networks was suggested and explained in detail. The AlN:Yb3+, Er3+ nanowire networks exhibit the weak green (around 523 and 545 nm) and very intense red (around 662 nm) emissions under 980 nm excitation, which is caused by the 2H11/2,4S3/2 and4F9/2 -> 4I15/2 transitions of Er3+ ions, respectively. The enhanced red emission is mainly due to the cross relaxation resulting from the high doping concentration. In the wide temperature range of 298-548 K, the integrated intensity of red emission varies linearly with temperature, which has a potential application for optical thermometry.
What problem does this paper attempt to address?